Abstract:Alumina materials have widely been used in industrial fields, such as catalysis and adsorption. However, due to the fast sol-gel process and complicated crystalline-phase transformation, the synthesis of alumina materials with both highly ordered mesostructures and crystallized frameworks remains a great challenge. Herein, we report a novel vesicle-aggregation-assembly strategy to prepare highly ordered mesoporous gamma-alumina microspheres with unique shifted double-diamond networks for the first time, by using diblock copolymer poly(ethylene oxide)-b-poly(methyl methacrylate) (PEO-b-PMMA) as a template and aluminum isopropoxide as a precursor in a tetrahydrofuran (THF)/hydrochloric acid binary solvent. During the gradual evaporation of THF and H2O, the as-made Al3+-based gel/PEO-b-PMMA composites can be obtained through a co-assembly process based on the hydrogen bonding interaction between hydroxyl groups of alumina oligomers and PEO segments of the diblock copolymers. The formed composites exhibit a spherical morphology with a wide size distribution (diameter size 1-12 mu m). Furthermore, these composite microspheres possess an inverse bicontinuous cubic mesostructure (double diamond, Pn (3) over barm) with Al3+-based gel buried in the PEO-b-PMMA matrix in the form of two intertwined but disconnected networks. After a simple calcination at 900 degrees C in air, the structure of the resultant mesoporous alumina changes to a relatively low symmetry (shifted double diamond, Fd (3) over barm), ascribed to the shifting of the two alumina networks due to loss of the templates. Meanwhile, the unit cell size of the alumina mesostructure decreases from similar to 131 to similar to 95 nm. The obtained ordered mesoporous alumina products retain the spherical morphology and possess ultra-large mesopores (similar to 72.8 nm), columnar frameworks composed of gamma-alumina nanocrystalline particles (crystal size of similar to 15 nm) and high thermal stability (up to 900 degrees C). As a support of Au nanoparticles, the formed Au/mesoporous gamma-alumina composite catalysts have been used in the catalytic reduction of 4-nitrophenol with a high kinetic constant k of 0.0888 min(-1), implying promising potential as a catalyst support.

Preparation and properties of the Al2O3–SiO2 aerogel/alumina framework composite

Preparation and properties of hierarchical structural alumina/mullite composites

Preparation and Characterization of C/Al 2 O 3 Composite Aerogel with High Compressive Strength and Low Thermal Conductivity

Novel Al2O3–SiO2 composite aerogels with high specific surface area at elevated temperatures with different alumina/silica molar ratios prepared by a non-alkoxide sol–gel method

Robust monolithic polymer(resorcinol-formaldehyde) reinforced alumina aerogel composites with mutually interpenetrating networks

Synthesis and characterization of SiO2-Al2O3 composite aerogel using inorganic aluminum salt as raw material

Synthesis of a novel Al 2 O 3 –SiO 2 composite aerogel with high specific surface area at elevated temperatures using inexpensive inorganic salt of aluminum

Preparation and Characterization of Alumina-coated Hollow Quartz Fiber Reinforced Al2O3-SiO2 Aerogel Composite

Facile synthesis of mullite fiber/alumina composite aerogel with enhanced bending strength and controllable thermal insulation performance

Synthesis of High-Surface-Area Alumina Aerogels without the Use of Alkoxide Precursors

Organic/inorganic double-precursor cross-linked alumina aerogel with high specific surface area and high-temperature resistance

Highly thermally stable zirconia/silica composite aerogels prepared by supercritical deposition

Preparation of Alumina Aerogel via Supercritical Method

Synthesis of Alumina Aerogels by Ambient Drying Method and Control of Their Structures

Fabrication of SiCN(O) Aerogel Composites with Low Thermal Conductivity by Wrapping Mesoporous Aerogel Structures over Mullite Fibers

Fabrication of the SiC/HfC Composite Aerogel with Ultra-Low Thermal Conductivity and Excellent Compressive Strength

Synthesis of monolithic aerogel-like alumina via the accumulation of mesoporous hollow microspheres

A vesicle-aggregation-assembly approach to highly ordered mesoporous γ-alumina microspheres with shifted double-diamond networks.

Rapid preparation of Palygorskite/Al2O3 composite aerogels with superhydrophobicity, high-temperature thermal insulation and improved mechanical properties

Fiber-Reinforced Coal Gangue-Based Alumina Aerogel Composites with Highly Thermal Stability by Ambient Pressure Drying

Fabrication of Al2O3 aerogel-SiO2 fiber composite with enhanced thermal insulation and high heat resistance