Abstract:Alumina materials have widely been used in industrial fields, such as catalysis and adsorption. However, due to the fast sol-gel process and complicated crystalline-phase transformation, the synthesis of alumina materials with both highly ordered mesostructures and crystallized frameworks remains a great challenge. Herein, we report a novel vesicle-aggregation-assembly strategy to prepare highly ordered mesoporous gamma-alumina microspheres with unique shifted double-diamond networks for the first time, by using diblock copolymer poly(ethylene oxide)-b-poly(methyl methacrylate) (PEO-b-PMMA) as a template and aluminum isopropoxide as a precursor in a tetrahydrofuran (THF)/hydrochloric acid binary solvent. During the gradual evaporation of THF and H2O, the as-made Al3+-based gel/PEO-b-PMMA composites can be obtained through a co-assembly process based on the hydrogen bonding interaction between hydroxyl groups of alumina oligomers and PEO segments of the diblock copolymers. The formed composites exhibit a spherical morphology with a wide size distribution (diameter size 1-12 mu m). Furthermore, these composite microspheres possess an inverse bicontinuous cubic mesostructure (double diamond, Pn (3) over barm) with Al3+-based gel buried in the PEO-b-PMMA matrix in the form of two intertwined but disconnected networks. After a simple calcination at 900 degrees C in air, the structure of the resultant mesoporous alumina changes to a relatively low symmetry (shifted double diamond, Fd (3) over barm), ascribed to the shifting of the two alumina networks due to loss of the templates. Meanwhile, the unit cell size of the alumina mesostructure decreases from similar to 131 to similar to 95 nm. The obtained ordered mesoporous alumina products retain the spherical morphology and possess ultra-large mesopores (similar to 72.8 nm), columnar frameworks composed of gamma-alumina nanocrystalline particles (crystal size of similar to 15 nm) and high thermal stability (up to 900 degrees C). As a support of Au nanoparticles, the formed Au/mesoporous gamma-alumina composite catalysts have been used in the catalytic reduction of 4-nitrophenol with a high kinetic constant k of 0.0888 min(-1), implying promising potential as a catalyst support.

Synthesis of monolithic aerogel-like alumina via the accumulation of mesoporous hollow microspheres

Synthesis of Alumina Aerogels by Ambient Drying Method and Control of Their Structures

Synthesis of a novel Al 2 O 3 –SiO 2 composite aerogel with high specific surface area at elevated temperatures using inexpensive inorganic salt of aluminum

Synthesis of High-Surface-Area Alumina Aerogels without the Use of Alkoxide Precursors

Preparation of Alumina Aerogel via Supercritical Method

Novel Al2O3–SiO2 composite aerogels with high specific surface area at elevated temperatures with different alumina/silica molar ratios prepared by a non-alkoxide sol–gel method

Synthesis and characterization of SiO2-Al2O3 composite aerogel using inorganic aluminum salt as raw material

Synthesis of alumina aerogel enriched carboxymethyl cellulose with polymodal pore size distribution by ambient pressure drying

Fabrication and characterization of the monolithic hydrophobic alumina aerogels

A Facile Method to Fabricate Al2O3-SiO2 Aerogels with Low Shrinkage up to 1200 °C

Highly Thermally Stable Alumina-Based Aerogels Modified by Partially Hydrolyzed Aluminum Tri-Sec-butoxide

One-step Synthesis of Monolithic Micro-Nano Yttria Stabilized ZrO2-Al2O3 Composite Aerogel

Fabrication and Thermal Stability of La2O3 Doped Alumina Aerogel

Facile synthesis of mullite fiber/alumina composite aerogel with enhanced bending strength and controllable thermal insulation performance

Synthesis of Al2O3-SiO2 aerogels with low thermal conductivity and high strength by methyltriethoxysilane as a silica precursor

Preparation and Characterization of Hydrophobic Mesoporous SiO2 Aerogel

Preparation of monolithic Al2O3–SiO2 aerogels with high-temperature resistance using boehmite nanorods

Organic/inorganic double-precursor cross-linked alumina aerogel with high specific surface area and high-temperature resistance

A vesicle-aggregation-assembly approach to highly ordered mesoporous γ-alumina microspheres with shifted double-diamond networks.

Preparation and Characterization of Alumina-coated Hollow Quartz Fiber Reinforced Al2O3-SiO2 Aerogel Composite

Preparation of High-Temperature Resistant Aerogels by Incorporating Aluminum Sol into Composite Silica Sources Using Ambient Pressure Drying