Abstract:The preparation of monolithic silica aerogels via non-supercritical drying is realized by the following procedures: (1) formation of silica alcogels with perfect network structure by controlling two-step hydrolysis and condensation reaction rates of tetraethoxysilane; (2) improvement and reinforcement of network structure and strength of silica gels through exchanging the pore fluid with ethanol solvent thoroughly, immersing of gels in the ethanol solutions of tetraethyoxysilane and aging; (3) gradual drying under ethanol fluid whose surface tension is much lower than water under ambient pressure. The resulting aerogels were characterized by means of SEM, TEM, TG-DTA, XRD, and adsorption-desorption techniques. It is found that the aerogels, which are made up of uniform spherical nanoparticles with diameters of about 10 nm, are of coherent network structures. Furthermore, the aerogels are porous, and the porosity is as high as 91%. The diameter of the pore sizes is in the range of 10 similar to 30 nm, and the density of the aerogels is low (200 similar to 400 kg . m(-3)). The specific surface area of the aerogels can be as high as 625. 65 m(2) . g(-1). The appearance, microstructure, diameters of primary particles and pore size distributions of the aerogels are in concordance with those prepared by conventional supercritical drying. It is demonstrated that the quality of the resulting aerogels is affected by the preparation conditions adopted in the preparation process. In fact, by adjusting the proportions of the reaction systems, and controlling the adding amounts of acid and base during the two-step hydrolysis and condensation process, silica aerogels with required density, definite strength and ideal morphology can be produced.

Preparation of monolithic Al2O3–SiO2 aerogels with high-temperature resistance using boehmite nanorods

Hydrothermal assisted synthesis of heat resistant, well-crystallized aerogels constructed by boehmite nano rods

Novel silica-modified boehmite aerogels and fiber-reinforced insulation composites with ultra-high thermal stability and low thermal conductivity

Synthesis and Thermal Behavior of High-Surface-Area Monolithic Alumina Aerogels

Alumina-Doped Silica Aerogels for High-Temperature Thermal Insulation

A Facile Method to Fabricate Al2O3-SiO2 Aerogels with Low Shrinkage up to 1200 °C

Reusable, High Specific Surface Areas, and Excellent Thermal Stability Al2O3–SiO2 Aerogel Composites As High-Temperature Thermal Insulators for Radome Applications

Preparation of Silica Aerogels Via Non-supercritical Drying and Their Formation Process

Preparation and properties of aluminosilicate aerogels from boehmite and waterglass

Heat-resistant, strong alumina-modified silica aerogel fabricated by impregnating silicon oxycarbide aerogel with boehmite sol

Facile One-Step Precursor-to-aerogel Synthesis of Silica-Doped Alumina Aerogels with High Specific Surface Area at Elevated Temperatures

A Facile Method to Fabricate Monolithic Alumina–silica Aerogels with High Surface Areas and Good Mechanical Properties

Preparation and characterization of monolithic alumina aerogels

Ultralight, thermal insulating, and high-temperature-resistant mullite-based nanofibrous aerogels

Novel Al2O3–SiO2 composite aerogels with high specific surface area at elevated temperatures with different alumina/silica molar ratios prepared by a non-alkoxide sol–gel method

Synthesis of Al2O3-SiO2 aerogels with low thermal conductivity and high strength by methyltriethoxysilane as a silica precursor

Preparation and High Temperature Inorganic Transformation of Flexible Silicone Aerogels

Synthesis of a novel Al 2 O 3 –SiO 2 composite aerogel with high specific surface area at elevated temperatures using inexpensive inorganic salt of aluminum

Design and preparation of novel Y2O3-SiO2 composite aerogels for high-temperature thermal insulators

Nanoengineering Super Heat-Resistant, Strong Alumina Aerogels

Preparation and properties of low-density and high-temperature resistant yttrium doped silica aerogels