Abstract:Si3N4 aerogel, which is one of the most promising materials for application as high-temperature thermal insulation, is synthesized by the urea-assisted sol-gel technique, followed by the supercritical drying, carbonization, carbothermal reduction and carbon combustion processes. The effects of heat treatment temperatures on the physicochemical and textural evolution of mesoporous Si3N4 aerogel are investigated. Si3N4 aerogel is formed when the heat treatment temperature increases to 1500 degrees C, whereas it transforms into SiC phase with a further higher temperature of 1600 degrees C. The SEM analysis confirms the existence of Si3N4 nanoparticles, and the particle size of Si3N4 nanoparticles is around 20-40 nm, with pore size around 20-40 nm. The XPS measurement reveals that Si3N4 aerogel is composed of 74.4% Si3N4 phase, with lower content of 25.6% SiO2. codoped aerogel possesses a large BET specific surface area of 519.6 m(2)/g, which results from the mesoporous pores left after carbon combustion. This value is much larger than that of the conventional Si3N4 porous ceramics and Si3N4 nano materials ever reported. The BJH adsorption average pore diameter of Si3N4 aerogel is around 11.8 nm, with a large pore volume of 3.5 cm(3)/g. Si3N4 oxidation with forming amorphous SiO2 layer on the surface is observed by the TG measurement. Moreover, the resulting Si3N4 aerogel shows low bulk density of 0.075 g/cm(3), as well as low thermal conductivity of 0.045 W/(m.K) at room temperature. The mechanism of Si3N4 formation is based on the VS growth between C, SiO2 and N-2. The structures evolution and formation mechanism of Si3N4 aerogel are also investigated in this study.

Synthesis of a novel Al 2 O 3 –SiO 2 composite aerogel with high specific surface area at elevated temperatures using inexpensive inorganic salt of aluminum

Novel Al2O3–SiO2 composite aerogels with high specific surface area at elevated temperatures with different alumina/silica molar ratios prepared by a non-alkoxide sol–gel method

Synthesis and characterization of SiO2-Al2O3 composite aerogel using inorganic aluminum salt as raw material

A Facile Method to Fabricate Al2O3-SiO2 Aerogels with Low Shrinkage up to 1200 °C

Synthesis and Thermal Behavior of High-Surface-Area Monolithic Alumina Aerogels

A Facile Method to Fabricate Monolithic Alumina–silica Aerogels with High Surface Areas and Good Mechanical Properties

Heat-resistant, strong alumina-modified silica aerogel fabricated by impregnating silicon oxycarbide aerogel with boehmite sol

Synthesis of monolithic aerogel-like alumina via the accumulation of mesoporous hollow microspheres

Synthesis of Al2O3-SiO2 aerogels with low thermal conductivity and high strength by methyltriethoxysilane as a silica precursor

Preparation of Heat-Resistant Silica/Alumina Composite Aerogel by Adding Trimethylethoxysilane

Preparation of High-Temperature Resistant Aerogels by Incorporating Aluminum Sol into Composite Silica Sources Using Ambient Pressure Drying

Synthesis and Characterization of Silica Aerogel and Its Composite Materials

Synthesis Of Nanoporous Sio2 Areogel Microsphere Materials

Synthesis and Textural Evolution of Mesoporous Si3N4 Aerogel with High Specific Surface Area and Excellent Thermal Insulation Property Via the Urea Assisted Sol-Gel Technique

Facile One-Step Precursor-to-aerogel Synthesis of Silica-Doped Alumina Aerogels with High Specific Surface Area at Elevated Temperatures

Preparation and Thermal Stablity of Silica- alumina-fibers Composite Aerogels

Fabrication of Al2O3 aerogel-SiO2 fiber composite with enhanced thermal insulation and high heat resistance

Design and preparation of novel Y2O3-SiO2 composite aerogels for high-temperature thermal insulators

Preparation and Properties of Al2O3-SiO2 Aerogels

Preparation of monolithic Al2O3–SiO2 aerogels with high-temperature resistance using boehmite nanorods

Novel silica-modified boehmite aerogels and fiber-reinforced insulation composites with ultra-high thermal stability and low thermal conductivity