Abstract:Crack-free mesoporous equimolar Al2O3-SiO2-TiO2 ternary nanocomposite aerogel has been synthesized using an ethanol supercritical drying technique. The effects of heat treatment temperatures on its textural and structural evolution during thermal treatment are investigated in this study. XRD results reveal that only anatase phase is detected in the as-dried ternary aerogel, whereas peaks corresponding to silica and alumina phase are not shown due to its much faster polymerization rate of titania precursor. Structural transition from boehmite to γ-Al2O3 begins to occur at 450°C within the ternary aerogel, and this process is completed at nearly 615°C. The needle-like reticulated γ-Al2O3 grows along the anatase backbone, however, it is not evident in the XRD patterns. The morphologies of the ternary aerogel become more homogeneous after the structural transition, as indicated by the SEM analysis, which is also consistent with the BET results. With the increase of heat temperature up to 1050°C, the γ-Al2O3 phase disappears and no separate SiO2 is detected. At the same time, the silica-alumina network originates in a structure of Al-O-Si, and the silicon atoms incorporate into the alumina phase in the γ-Al2O3 structure, disordering the alumina primary particles. When the heat treatment temperature increases to 1200°C, mullitization begins to occur along the titania backbone, whereas silica crystallization happens at 1300°C. The 600°C calcinated ternary aerogel is typically mesoporous, showing high specific surface area (255.37m2/g), suitable average pore diameter (22.83nm) and large pore volume (1.34cm3/g). Moreover, the ternary aerogels show high surface acid activity at temperatures below 1000°C, which have future applications for ideal catalysts and catalyst supports at elevated temperatures.

Synthesis and characterization of SiO2-Al2O3 composite aerogel using inorganic aluminum salt as raw material

Synthesis of a novel Al 2 O 3 –SiO 2 composite aerogel with high specific surface area at elevated temperatures using inexpensive inorganic salt of aluminum

Novel Al2O3–SiO2 composite aerogels with high specific surface area at elevated temperatures with different alumina/silica molar ratios prepared by a non-alkoxide sol–gel method

Preparation of Alumina Aerogel via Supercritical Method

Preparation of High-Temperature Resistant Aerogels by Incorporating Aluminum Sol into Composite Silica Sources Using Ambient Pressure Drying

Preparation and Characterization of C/Al 2 O 3 Composite Aerogel with High Compressive Strength and Low Thermal Conductivity

Preparation and Characterization of Alumina-coated Hollow Quartz Fiber Reinforced Al2O3-SiO2 Aerogel Composite

Synthesis of Al2O3-SiO2 aerogels with low thermal conductivity and high strength by methyltriethoxysilane as a silica precursor

A Facile Method to Fabricate Al2O3-SiO2 Aerogels with Low Shrinkage up to 1200 °C

Synthesis of monolithic aerogel-like alumina via the accumulation of mesoporous hollow microspheres

Preparation and Characterization of Hydrophobic Mesoporous SiO2 Aerogel

Fabrication of Al2O3 aerogel-SiO2 fiber composite with enhanced thermal insulation and high heat resistance

Synthesis and Textural Evolution of Mesoporous Si3N4 Aerogel with High Specific Surface Area and Excellent Thermal Insulation Property Via the Urea Assisted Sol-Gel Technique

Design and preparation of novel Y2O3-SiO2 composite aerogels for high-temperature thermal insulators

Investigation on textural and structural evolution of the novel crack-free equimolar Al2O3-SiO2-TiO2 ternary aerogel during thermal treatment

Fabrication and Thermal Stability of La2O3 Doped Alumina Aerogel

Synthesis of Alumina Aerogels by Ambient Drying Method and Control of Their Structures

Preparation and Structural Evolution of SiOC Preceramic Aerogel During High-Temperature Treatment

Preparation and Thermo-Mechanical Properties of Modified Gelatin Reinforced SiO2 Aerogels

Preparation and properties of the Al2O3–SiO2 aerogel/alumina framework composite

One-step Synthesis of Monolithic Micro-Nano Yttria Stabilized ZrO2-Al2O3 Composite Aerogel