Abstract:Hierarchical structural alumina/mullite composites constructed by alumina platelets inter-locked porous matrices and mullite whiskers secondary structures had been designed and prepared based on the fluorine-catalyzed gas-phase process. In the composites, mullite whiskers grew on the alumina platelets of the matrices to form cactus-like structures, before that, topaz rods as transitional secondary structures formed at lower temperature. The fluorine-etching effects on secondary structures' nucleation were discussed. The alumina/mullite composites (1300 o C) had low bulk density (1.10 g/cm 3 ), high porosity (71.4%), and proper compression strength (~14.2 MPa), meanwhile, the average filtration efficiencies of PM2.5 and PM10 during the filtration tests were 78% and 76%, respectively. The introduced mullite whiskers with length of ~1 μm had not induced obvious changes on the structural parameters, hence, the alumina/mullite composites (1300 o C) possessed similar particle filtration performances compared with the alumina porous matrices, and both of the two species materials could be applied for hot gas filtration.

Preparation and properties of hierarchical structural alumina/mullite composites