SHS of Al_2O_3+TiB_2/NiAl Compound Composites
HEI hong-jun,CUI hong-zhi,XIE yan-chun,ZHANG jin-ling,CAO li-li,ZHANG hai-bo
2007-01-01
Abstract:Al2O3+TiB2 composite ceramic materials have much more excellent performances: high hardness,high melting-point,high-thermal conductivity,low-expansion coefficient,high-wearing feature,pyrochemistry stability and so on,which metal material is unable to achieve.But both of them belong to hard brittle materials,they still have some shortcomings,just as high brittleness,strong crack-sensitivity,weak of mechanical impact properties and temperature deformation.In order to improve these shortcomings,in this page NiAl and FeAl intermetallic compounds were appended to the composite ceramics.As the result of the XRD picture,Al2O3+TiB2,Al2O3+TiB2+NiAl and Al2O3+TiB2+FeAl are the major phase composition,which indicated that SHS reactions were thoroughly processed.Over passing the comparison of the density,hardness and fracture toughness property of the reaction products with different component,the tiptop of the density is 99.5% when the content of FeAl is 15%,while it is 98.5% when the content of NiAl is 20%.The more content of NiAl and FeAl intermetallic compound,the lower hardness and the higher fracture toughness of the synthetical composites.