Abstract:Al2O3p/Al composites were prepared by direct melt reaction process. The thermodynamics of in situ chemical reactions between molten aluminum and CeO2 powder was studied. The XRD results show that the components of the as-prepared composites consist of Al2O3 and Al phases. For the as-cast composite specimens, SEM, EDX, TEM and SAD were used to analyze the reinforcement phases and interface characters of composites. The results show that the in situ generated Al2O3 particles, whose sizes are 100–200nm, have various irregular shapes and disperse uniformly in matrix. TEM observation shows that the interface between particle and matrix is clean. Furthermore, there is no fixed orientation relationship between Al2O3 particles and aluminum matrix. Only [12¯10]//[111] orientation parallel relationship with low exponent is found. Therefore, the composites have isotropic properties. Besides characters mentioned above, there are large amount of high density dislocations and the generated extensive fine subgrains around Al2O3 particles. These features are favorable for improving composite performances. As a result, the composites are comprehensively strengthened not only by Al2O3 particles, but also by the high density dislocations and fine subgrains.

Evaluation of the microstructure of in-situ reaction processed Al3Ti-Al2O3-Al composite

In Situal3ti–al2o3 Intermetallic Matrix Composite: Synthesis, Microstructure, and Compressive Behavior

FLEXURAL STRENGTH OF IN-SITU REACTION PROCESSED Al2O3-Al3Ti-Al COMPOSITES

Microstructure and properties of in-situ reaction Al/Al3 Ti composite

Reaction Procedure of a Graphite Fiber Reinforced Ti-Al Composite Produced by Squeeze Casting- in Situ Reaction

Microstructure Evolution of Ti-Al-C System Composite

Processing of in situ aluminum-matrix composites and controlling of the solidification microstructures

Study on Ti Fiber Reinforced Tial3 Composite by Infiltration-In Situ Reaction

In Situ Fabrication and Properties of (Al3Ti)P/6351 Composites

Preparation and properties of Al2O3/Al-2(1-0.2)Mg0.2Ti(1+0.2)O5 matrix ceramic composite

Fabrication of in situ Al3Ti/Al composites by using ultrasound assisted direct reaction between solid Ti powders and liquid Al

Microstructure of Ti3AI Intermetallic Matrix Composites Produced by In-Situ Reaction

Synthesis of C F /tial 3 Composite by Infiltration-In Situ Reaction

Microstructure of in Situ Al3Ti/6351Al Composites Fabricated with Electromagnetic Stirring and Fluxes

In-Situ Preparation of Al/Tial3(P) Composite by Direct Reaction Between Molten Al and Tio2 Powder

Microstructural characterization and mechanical properties of TiAl–Al2Ti4C2–Al2O3–TiC in situ composites by hot-press-aided reaction synthesis

In Situ Formation of Al3Ti and Its Effects on the Microstructure, Hardness and Tribological Properties of Al Matrix Composites with Various Ti Contents

In situ fabrication and microstructure of Al2O3 particles reinforced aluminum matrix composites

Microstructure and property of Al/TiC composites prepared by reaction synthesis

Microstructure Formation Mechanism of (al2o3+tib2+al3ti)/al Composites Fabricated by Reactive Hot Pressing

Reaction synthesis, microstructure, and mechanical properties of in-situ TiAl-based multiphase composites