Abstract:TiAl intermetallic compounds, as a new kind of high-performance light-weight structural material, are widely applied in many fields. Titanium carbide (TiC) as the reinforcing phase could improve the mechanical properties, wear resistance, and heat-resistance stability of TiAl intermetallic compounds. Ti(Al, C) mixture powders were deposited by cold spraying at gas temperature of 250 °C, 450 °C, and 550 °C. Then, Ti(Al, C) coatings were annealed at temperatures of 650 °C for different times and following holding at 1100 °C for 3 h. The microstructure, microhardness, fracture toughness, and abrasive wear of Ti-Al composite coatings were investigated. The research results were that the particle size of mixture powders decreased as the ball milling time prolonging. Ti(Al) solid solution appeared in the mixture powders as the milling time increased to 30 h. The average porosity of the coating sprayed at 550 °C was the lowest (0.85%). The as-sprayed coatings exhibited the same phase compositions with the mixture powders. The coating sprayed at gas temperature of 550 °C has the highest microhardness and the lowest weight loss. Ti-Al intermetallic was in-situ synthesized after annealing at 650 °C. The average porosity of the annealed coating (sprayed at 450 °C) was the lowest. The content of Ti-Al intermetallic compounds of the annealed coating sprayed at 450 °C is the highest. The X-ray diffraction (XRD) analysis results are consistent with the EDS analysis of the annealed coatings after annealing at 650 °C. Ti-Al intermetallic compounds were almost completely formed in the three kinds of the coatings after annealing at 650 °C for 20 h and following holding at 1100 °C for 3 h. TiAl and TiAl3 intermetallic phases were in-situ synthesized in the coatings based on the energy dispersive spectroscopy (EDS) and XRD analysis. TiC was also in situ synthesized in the coatings as the annealing temperature increased to 1100 °C. The annealed coating (sprayed at 450 °C) has the highest microhardness, fracture toughness, and wear resistance properties after annealing at 1100 °C for 3 h.

In-situ Production and Microstructure of TiC/Fe3 Al Composites

In Situal3ti–al2o3 Intermetallic Matrix Composite: Synthesis, Microstructure, and Compressive Behavior

Preparation, Microstructure and Mechanical Properties of In-Situ TiC/Al–Si–Fe Aluminum Matrix Composites

Reaction mechanism and microstructure evolution of superhigh strength in-situ TiC/Ti composite based on Cr 2 AlC-Ti system

Microstructure and mechanical properties of Al2O 3/TiAl in situ composites doped with Fe2O3

In-situ TiC/Ti composites based on Ti 2 AlC–Ti system: Reaction process, microstructure, and mechanical properties

Microstructure and Mechanical Properties of Ti2AlC-reinforced TiAl Composites

Preparation of Ti/Al based nanophase composite powder by mechanical alloying

Preparation of ti-al based nanophase composite powder by mechanical alloying

Microstructural Characterization of TiC-White Cast-Iron Composites Fabricated by In Situ Technique

Microstructure and mechanical properties of in-situ TiC hybrid reinforced TC4 matrix composites by a new additive manufacturing method

Investigation on microstructure and properties of TiC0.5-Al2O3/Cu composites fabricated by a novel in-situ reactive synthesis

Microstructural characterization and mechanical properties of (TiC+TiB)/TA15 composites prepared by an in-situ synthesis method

Microstructure evolution, mechanical properties, and wear behavior of in-situ TiCx/TC4 composites

Microstructure, Microhardness, Fracture Toughness, and Abrasive Wear of In-Situ Synthesized TiC/Ti-Al Composite Coatings by Cold Spraying Combined with Heat Treatment

Microstructure, mechanical properties and strengthening mechanism of in-situ synthesized TiC/6061 nanocomposites

In-Situ Synthesis, Microstructure, and Mechanical Properties of TiB2-Reinforced Fe-Cr-Mn-Al Steel Matrix Composites Prepared by Spark Plasma Sintering

Evaluation of the microstructure of in-situ reaction processed Al3Ti-Al2O3-Al composite

The effect of carbon source and molar ratio in Fe–Ti–C system on the microstructure and mechanical properties of in situ TiC/Fe composites

Microstructure and Mechanical Properties of Al<sub>2</sub>O<sub>3</sub>/TiAl <i>In Situ</i> Composites Doped with Fe<sub>2</sub>O<sub>3</sub>

In Situ Formation of Al3Ti and Its Effects on the Microstructure, Hardness and Tribological Properties of Al Matrix Composites with Various Ti Contents