Abstract:In this paper, dense MAX phase Ti3AlC2 enhanced and toughened TiAl3 matrix composites with mass fractions of 10∼40% were prepared by in-situ reaction via powder metallurgy route which using TiH2, Al and TiC powder as the starting materials. Then, the microstructure and phase structure of the composites were characterized, and the relationship between microstructure, mechanical properties and fracture mechanism was systematically investigated. The results show that the lath-like (micron level) and fine-needle-like (submicron level) reinforcements Ti3AlC2 are uniformly distributed in TiAl3 matrix. With the increases of mass fraction of reinforcements, the average grain size of the TiAl3 matrix decreases remarkably from 7.6 μm to 4.8 μm, indicating that the reinforcements Ti3AlC2 can effectively refine the matrix grains and plays a good pinning effect on the TiAl3 matrix. The prepared Ti3AlC2/TiAl3 composite with 30% mass fraction exhibits excellent comprehensive mechanical properties: the Vickers hardness, flexural strength, fracture toughness is 575 ± 5 HV, 470 ± 18 MPa, and 3.83 ± 0.05 MPa m1/2, 14.1%, 174.9% and 117.6% higher than that of the pure TiAl3 matrix, respectively. Both the strengthening and toughening effects are significant. The strengthening mechanism are fine grain strengthening and deformation strengthening, while the toughening mechanism is a synthetic effect in terms of crack deflection, crack bifurcation, grain refinement and stress-induced microcrack. Fracture analysis shows that the fracture mechanism is transgranular (cleavage) fracture.

Processing, Microstructural Characterization and Mechanical Properties of in Situ Ti3AlC2/TiAl3 Composite by Hot Pressing

Microstructure and mechanical properties of Ti3(Al,Ga)C2/Al2O3 composites prepared by in situ reactive hot pressing

Microstructure and Mechanical Properties of Ti2AlC-reinforced TiAl Composites

In Situal3ti–al2o3 Intermetallic Matrix Composite: Synthesis, Microstructure, and Compressive Behavior

Preparation and characteristics of Ti3AlC2 -Al3Ti/Al composite materials synthesized from pure Al and Ti3AlC2 powders

FLEXURAL STRENGTH OF IN-SITU REACTION PROCESSED Al2O3-Al3Ti-Al COMPOSITES

Design and Strengthening Behaviour of Ti2alc/Tial Composite by Low-Temperature Hot-Pressing Process

In Situ TiBw/Ti–6Al–4V Composites with Novel Reinforcement Architecture Fabricated by Reaction Hot Pressing

In-situ TiC/Ti composites based on Ti 2 AlC–Ti system: Reaction process, microstructure, and mechanical properties

Tailoring Ultrafine Grained and Dispersion-Strengthened Ti2AlC/TiAl Composite Via a New Fabrication Route

Synthesis and Mechanical Properties of TiB2/Ti2AlN Composites Fabricated by Hot Pressing Sintering

Preparation and toughness mechanism of in-situ Ti3AlC2 enhanced and toughened TiAl3 matrix composites

Effect of Heat Treatment on the Microstructure and Properties of Ti3AlC2-Cr2AlC-TiC Composite

Reaction mechanism and microstructure evolution of superhigh strength in-situ TiC/Ti composite based on Cr 2 AlC-Ti system

Revealing the formation, strengthening and toughening mechanism of a new (Ti3AlC2+Al2O3)p /Al3Ti composite with strength-ductility synergy

Strengthening Ti3AlC2 by in Situ Synthesizing Ti3AlC2–Y4Al2O9 Composites

Fabrication of Al2O3–Ti3SiC2 Composites and Mechanical Properties Evaluation

Mechanical Properties and Microstructure of Al<sub>2</sub>O<sub>3</sub>-Ti<sub>3</sub>SiC<sub>2</sub> Ceramic Composites

In Situ Formation of Al3Ti and Its Effects on the Microstructure, Hardness and Tribological Properties of Al Matrix Composites with Various Ti Contents

Mechanical Properties and Microstructure of Al2o3/Tial in Situ Composites Doped with Cr2o3

Interpenetrating microstructure and fracture mechanism of NiAl/TiC composites by pressureless melt infiltration