Interpenetrating microstructure and fracture mechanism of NiAl/TiC composites by pressureless melt infiltration

M.X Gao,Y Pan,F.J Oliveira,J.L Baptista,J.M Vieira

DOI: https://doi.org/10.1016/j.matlet.2003.10.060

IF: 3

2004-01-01

Materials Letters

Abstract:NiAl/TiC composites with TiC content of 86–92 vol.% were prepared by pressureless melt infiltration. The high content of TiC and consequent TiC particles joining were obtained by pre-sintering of the as-pressed TiC preform before infiltration. Mechanical properties including bending strength, Vickers hardness, fracture toughness and Young's modulus were measured. The microstructure of the composites is characterized by the three-dimensional interpenetration of TiC and NiAl phases. Four-point bending strength and Vickers indentation hardness of NiAl/86 vol.%TiC composite are as high as 670±80 MPa and 14.0 GPa, respectively. This has been attributed to the characters of the microstructure such as the two interpenetrating phases , a high densification degree and freedom of defects as well. The fracture surface observed by SEM shows a dominant brittle fracture with somehow a ductile deformation in some thin NiAl ligaments. The thin NiAl ligament in the composites acts as crack bridge during fracture evidenced by indentation test.