Abstract:A novel molten-salt-mediated magnesiothermic reduction method was used to prepare 2H-SiC ultrafine powders by using silicon dioxide, active carbon and magnesium powders as raw materials. Phase compositions in the SiO2-2Mg-C system were thermodynamically evaluated by using the FactSage 6.2 package, and the effects of firing temperature, molar ratio of n(C)/n(Si) and amount of Mg on the synthesis of 2H-SiC powders were discussed. Phase compositions and microstructures of as-prepared ultrafine SiC powder were characterized by using X-ray diffraction (XRD), field emission gun scanning electron microscope (FE-SEM) and transmission electron microscope (TEM). SiO2 could be completely converted into SiC after 3 h at 1073 K, this temperature was about 600 K lower than required by the conventional methods, and the relatively content of 2H-SiC in the final SiC sample reached about 45 wt%. Furthermore, the content of 2H-SiC could be increased to 72 wt% upon firing at 1373 K for 3 h and using about 60 wt% excessive Mg. In contrast to this, only 20 wt% SiC was formed in the sample fired under the identical conditions but without using a molten salt medium. The average crystalline sizes of 2H-SiC in the product powders resultant from 3 h firing at 1073 and 1373 K were about 24 and 39 nm, respectively. A formation mechanism of SiC powder in the case of using molten-salt-mediated magnesiothermic reduction was proposed based on the experimental results.

Low Temperature Synthesis of 2H-Sic Powders Via Molten-Salt-Mediated Magnesiothermic Reduction

Studies of synthesizing the SiC nanometer powders by chemical vapor reaction

Optimization of Microstructure to Improve Si3n4 Ceramics with Thermal Conductivity and Mechanical Properties: Effect of Si and Α-Si3n4 Powder Composition

Fabrication of High‐purity HfSi2 Powder Via Molten Salt‐assisted Magnesium Thermal Reduction

Low-temperature pseudomorphic transformation of ordered hierarchical macro-mesoporous SiO2/C nanocomposite to SiC via magnesiothermic reduction.

Manipulation Of Phase And Microstructure At Nanoscale For Sic In Molten Salt Synthesis

In situ synthesis of Al2O3–SiC powders via molten-salt-assisted aluminum/carbothermal reduction method

Rapid Synthesis of SiC Powders by Spark Plasma-Assisted Carbothermal Reduction Reaction

Synthesis and microwave dielectric properties of (Ca0.7Mg0.3)SiO3 nanopowder prepared at low temperature

Synthesis of nanocrystalline silicon carbide powders

Low temperature Pr 3 Si 2 C 2 ‐assisted liquid phase sintering of SiC with improved thermal conductivity

In-situ Synthesis of Nanocrystalline TiC Powders, Nanorods, and Nanosheets in Molten Salt by Disproportionation Reaction of Ti(II) Species

Synthesis and formation mechanism of ZrC–SiC–TiC ceramic powders with high-sinterability via sol-gel process and carbothermal reduction

Low-temperature formation of nanocrystalline β-SiC with high surface area and mesoporosity via reaction of mesoporous carbon and silicon powder

Synthesis of Stoichiometric Titanium Carbide by a Combination of Carbothermal Reduction and Molten Salt Method and Its Characterization

Highly Efficient and Low-Temperature Preparation of Plate-Like ZrB₂-SiC Powders by a Molten-Salt and Microwave-Modified Boro/Carbothermal Reduction Method.

Synthesis of High Purity SiC Powder for High-resistivity SiC Single Crystals Growth

Densification and Enhancement of Sic Particulate Reinforced Fine Grain Sic Ceramic

Synthesis and investigation of the physicochemical properties of polymorphic 3C–SiC

Preparation Of Nanocrystalline Silicon Carbide Powders By Carbothermal Reduction

Temperature field regulation and growth mechanism of SiC fiber during microwave synthesis with catalyst assistance