Abstract:High purity silicon carbide (SiC) powder was synthesized in-situ by chemical reaction between silicon and carbon powder. In order to ensure that the impurity concentration of the resulting SiC powder is suitable for high-resistivity SiC single crystal growth, the preparation technology of SiC powder is different from that of SiC ceramic. The influence of the shape and size of carbon particles on the morphology and phase composition of the obtained SiC powder were discussed. The phase composition and morphology of the products were investigated by X-ray diffraction, Raman microspectroscopy and scanning electron microscopy. The results show that the composition of resulting SiC by in-situ synthesis from Si/C mixture strongly depends on the nature of the carbon source, which corresponds to the particle size and shape, as well as the preparation temperature. In the experimental conditions, flake graphite is more suitable for the synthesis of SiC powder than activated carbon because of its relatively smaller particle size and flake shape, which make the conversion more complete. The major phase composition of the full conversion products is belta-SiC, with traces of alpha-SiC. Glow discharge mass spectroscopy measurements indicated that SiC powder synthesized with this chemical reaction method can meet the purity demand for the growth of high-resistivity SiC single crystals.

Synthesis of nanocrystalline silicon carbide powders

Preparation Of Nanocrystalline Silicon Carbide Powders By Carbothermal Reduction

Studies of synthesizing the SiC nanometer powders by chemical vapor reaction

Low-temperature formation of nanocrystalline β-SiC with high surface area and mesoporosity via reaction of mesoporous carbon and silicon powder

Theoretical and experimental study of the mechanism for preparation of SiC nanowires by carbothermal reduction

Synthesis of Silicon Nitride/Silicon Carbide Nanocomposite Powders through Partial Reduction of Silicon Nitride by Pyrolyzed Carbon

Synthesis of High Purity SiC Powder for High-resistivity SiC Single Crystals Growth

Syntheses and Growth Mechanisms of 3C-Sic Nanostructures from Carbon and Silicon Powders.

Synthesis and Characterization of SiC Nanowires Through a Reduction−Carburization Route

Preparation Of Nanocrystalline Zirconium Carbide Powders By Carbothermal Reduction

A Simple Route to Nanocrystalline Silicon Carbide

Rapid Synthesis of SiC Powders by Spark Plasma-Assisted Carbothermal Reduction Reaction

A New Rapid Reduction−Carbonization Route to Nanocrystalline Β-Sic

Synthesis of Silicon Carbide Nanowires in a Catalyst-Assisted Process

Controlled growth of SiC crystals in combustion synthesis

Carbothermally prepared nanophase SiC/ Si3N4 composite powders and densified parts

Synthesis of SiC@SiO2 Nanocables Via a Catalyst-Free Carbothermal Reduction Method

Processing of Nanocrystalline Zirconium Carbide Powders

Synthesis of SiC-AlN Ceramic Alloy Powder by the Direct Reactions Between the Constituent Elements.

Synthesis and characterization of submicron silicon carbide powders with silicon and phenolic resin

Synthesis of monodisperse and high-purity α-Si3N4 powder by carbothermal reduction and nitridation