Abstract:The study covers the method of azide self-propagating high-temperature synthesis (SHS-Az) to obtain a highly dispersed TiN–SiC ceramic composite with a theoretical ratio of nitride and carbide phases from 1 : 4 to 4 : 1 (in moles) using the combustion of the corresponding composition of powder reagent mixtures: NaN 3 sodium azide, (NH 4 ) 2 TiF 6 , (NH 4 ) 2 SiF 6 and Na 2 SiF 6 halide salts, titanium, silicon and carbon in a nitrogen gas atmosphere. Thermodynamic calculations using the Thermo computer program showed that the optimum nitrogen pressure in the reactor is about 4 MPa, and the final composition of SHS-Az products can be completely different depending on the composition of reagents: it may include only target phases (TiN–SiC), contain silicon nitride and free carbon phases impurities (TiN–SiC–Si 3 N 4 –C) along with the target phases or consist only of nitride and free carbon phases (TiN–Si 3 N 4 –C). It was found that only target TiN and SiC phases are formed when using halide salt (NH 4 ) 2 TiF 6 , at any ratio of nitride and carbide phases in the final powder composition. In cases where halide salts (NH 4 ) 2 SiF 6 and Na 2 SiF 6 are used, target TiN and SiC phases are synthesized with an increased titanium content in reagents, i.e. only when composites of the 2TiN–SiC and 4TiN–SiC with an increased content nitride phase are obtained. Experimental studies of combustion products using scanning electron microscopy, energy dispersion analysis and X-ray phase analysis showed that they differ significantly from the theoretical compositions of products by the completely absent or significantly reduced SiC phase content in the final composition of powder composites synthesized during the combustion of bulk charge with carbon, and at the same time the absence of free carbon in the final composition of powder composites obtained. This difference is explained by the fact that when the combustion of a silicon and carbon powder mixture is initiated, silicon nitride is synthesized at the first stage with the temperature rising to high values of about over 1900 °C, at which the synthesized Si3N4 dissociates, and then at the second stage the resulting silicon reacts with carbon to form SiC that is more stable at high temperatures. But during combustion, very small light particles of carbon black (soot) may be removed (blown out) from a burning highly porous charge sample of bulk density by gases released at the first stage of combustion and not participate in the transformation of Si 3 N 4 into SiC. In this regard, in case of low-carbon charge combustion, silicon carbide either does not form at all, or it is formed in small quantities compared to the theoretically possible amount, and Si 3 N 4 silicon nitride remains the main component of the composite. A noticeable amount of SiC is formed only when burning high-carbon charges, but this amount is significantly less than the possible theoretical one, and the difference between them is replaced by the silicon nitride content. Therefore, it was experimentally shown for the first time that the SHS process can be used to obtain composites of highly dispersed ceramic powders TiN–Si 3 N 4 and TiN–Si 3 N 4 –SiC consisting of a mixture of nanoscale (less than 100 nm) and submicron (100 to 500 nm) particles with a relatively low content of free silicon admixture (less than 1.4 %).

Synthesis of Silicon Nitride/Silicon Carbide Nanocomposite Powders through Partial Reduction of Silicon Nitride by Pyrolyzed Carbon

Combustion Synthesis of Nanosized Β-Sic Powder on a Large Scale

Synthesis of nanocrystalline silicon carbide powders

Studies of synthesizing the SiC nanometer powders by chemical vapor reaction

Preparation Of Nanocrystalline Silicon Carbide Powders By Carbothermal Reduction

Carbothermally prepared nanophase SiC/ Si3N4 composite powders and densified parts

Preparation of Silicon Carbide Powder from Amorphous Silica and Investigation of Synthesis Mechanism

Synthesis of SiC-AlN Ceramic Alloy Powder by the Direct Reactions Between the Constituent Elements.

Synthesis and characterization of submicron silicon carbide powders with silicon and phenolic resin

Silicon oxycarbide composites reinforced with silicon nitride and in situ formed silicon carbide.

Synthesis and Consolidation of Composite Materials in the SiC–Si3N4–Si2N2O System

Improving the strength and oxidation resistance of phenolic resin derived pyrolytic carbons via Cu-catalyzed in-situ formation of SiC@SiO2

Preparation of SiC Powders by Carbothermal Reduction with Bamboo Charcoal As Renewable Carbon Source

Improving SiC grain growth and reducing carbon content in pyrolyzed polycarbosilane using nanosized Si particles

Azide self-propagating high-temperature synthesis of highly dispersed TiN–SiC ceramic nitride-carbide powder composites

Synthesis of High Purity SiC Powder for High-resistivity SiC Single Crystals Growth

Synthesis of monodisperse and high-purity α-Si3N4 powder by carbothermal reduction and nitridation

Synthesis and Characterization of Si/SiO2/SiC Composites Through Carbothermic Reduction of Rice Husk-based Silica

Combustion synthesis of α-Si3N4 powders using in-situ nano-SiO2 coated Si and Si3N4 reactants

Preparation of SiC-AlN Ceramic Alloy Powder by Direct Reaction Between Constituent Elements and Property Evaluation of Its Sintered Compacts.

Combustion synthesis of SiC/Al2O3 composite powders with SiC nanowires and their growth mechanism