Abstract:The non-oxide-reinforced phase AlN-SiC solid solution with high performance was successfully synthesized in the resin-bonded Al-Si-SiC composites under flowing nitrogen at 1300 °C. The AlN-SiC solid solution was synthesized by three paths of liquid-solid, gas-solid and gas-gas reactions through modulation of Al/Si ratio, and controllable microstructure of AlN-SiC solid solution was attained. The phase composition and microstructure of the sintered samples were characterized by XRD and SEM, combined with thermodynamics, the formation mechanism of AlN-SiC solid solution was investigated and the reaction model was established. Al was not detected while Si was detested by XRD. Granular, short columnar and whisker-like AlN-SiC solid solution were generated and their positions varied. As the temperature increases, the partial pressure of oxygen decreases due to the oxidation of Al, Si and SiC on the surface of the sample, inside the sample, the active oxidation takes place, generating Al2O(g), SiO(g) and CO(g). Due to the low oxygen partial pressure, Al is preferentially nitrided to form a thin AlN layer on its surface. The AlN layer is broken as the temperature increases, then liquid Al with carbon from resin begins to flow, leaving the residual shell of AlN in situ. When it flows to the surface of Si, Al-Sialloy is formed locally inside the Si particles under the wetting effect of C, then hexagonal AlN-SiC solid solution is formed inside the Si shell. Part of SiO(g) + CO(g) diffuses into the interior of the AlN residual shell and reacts by aggregation to form a granular AlN-SiC solid solution in the shell wall; others diffuses into the pores of the sample for vapor deposition, and finally forms stacked hexagonal flaky whiskers. The in-situ generated of AlN-SiC solid solution with multiple morphologies in the composite plays a joint toughening effect, which can significantly enhance the comprehensive performance of the composite. In this experiment, the synthesis of AlN-SiC solid solution without sintering aids under normal pressure at a low temperature. It is expected to be applied to the blast furnace and to realize the longevity of blast furnace.

Synthesis of SiC-AlN Ceramic Alloy Powder by the Direct Reactions Between the Constituent Elements.

Preparation of SiC-AlN Ceramic Alloy Powder by Direct Reaction Between Constituent Elements and Property Evaluation of Its Sintered Compacts.

Synthesis of SiC-AlN Powder and Characterization of Its HIP-Sintered Compacts.

Reaction Synthesis of SiC-AlN Ceramic Alloys

Preparation and mechanical properties of SiC-AlN ceramic alloy

Structural Formation and Mechanism in Combustion Synthesis of Nitrogen Ceramics (AIN, Si<sub>3</sub>N<sub>4</sub> and AIN-SiC)

Optimization of Microstructure to Improve Si3n4 Ceramics with Thermal Conductivity and Mechanical Properties: Effect of Si and Α-Si3n4 Powder Composition

Synthesis of SiC-AIN ceramic alloy by reaction sintering and its HIP-densification

Synthesis and Consolidation of Composite Materials in the SiC–Si3N4–Si2N2O System

Formation mechanism of AlN-SiC solid solution with multiple morphologies in Al-Si-SiC composites under flowing nitrogen at 1300 °C

Mechanical Properties of SiC-AlN Single-Phase Alloys and Two-Phase Composites.

Combustion synthesis of AlN-SIC solid solutions

Carbothermally prepared nanophase SiC/ Si3N4 composite powders and densified parts

Pressureless Sintering and High-Temperature Strength of SiC-AlN Ceramics

In-Situ Reactive Synthesis of AlN-SiC Composites and Solid Solutions

Sintering And Mechanical Properties Of Aln-Rich Ceramics In The Sic-Aln System

Studies of synthesizing the SiC nanometer powders by chemical vapor reaction

Synthesis mechanism of AlN–SiC solid solution reinforced Al2O3 composite by two-step nitriding of Al–Si3N4–Al2O3 compact at 1500 °C

In-situ synthesis of nano SiC particles in Al–Si–C system at 750 °C

Phase evolution mechanism of SiC-Al-Si composite under flowing nitrogen at 1600 °C

Hot Isostatically Pressed SiC‐AIN Powder Mixtures: Effect of Milling on Solid‐Solution Formation and Related Properties