Abstract:Features peculiar to the synthesis of SiC–Si 3 N 4 –Si 2 N 2 O composite powder with a controlled content of silicon carbide, nitride, and oxynitride phases, as well as the structure and properties of hot-pressed ceramics produced from this powder, were examined. The optimal composition of the synthesized SiC–Si 3 N 4 –Si 2 N 2 O powder was achieved by heating a 1 : 3 mixture of thermally expanded graphite (TEG) and silicon up to 1200°C in air. The interaction of TEG with fine silicon at 1200°C led to the formation of a solid solution of carbon in silicon carbide, accompanied by heat release. The generated heat increased temperature within localized volumes of the TEG cellular structure to a level where air nitrogen facilitated the development of silicon nitride and oxynitride and an amorphous phase. The amorphous phase crystallized as the interaction time increased to 2.5 h. The duration of the process influenced the final distribution of the phases, formed with the participation of CO, SiO, and air nitrogen. The microstructure of the synthesized powder was characterized by a general agglomerated state, resulting from rod and plate forms of Si 3 N 4 and Si 2 N 2 O. Hot pressing of the synthesized SiC–Si 3 N 4 –Si 2 N 2 O composite powder with Al 2 O 3 and Y 2 O 3 activators yielded superfine ceramics, possessing enhanced hardness and fracture toughness (HV10 = 20.7 GPa and K Ic = 6.5 MPa · m 1/2 ). The structure of the ceramics sintered at 2000°C differed from those sintered at 1850°C, primarily by higher density and average grain size. The superfine state significantly influenced the abrasive wear resistance of the ceramics in dry friction conditions. The linear wear index of a sample with an average size of structural elements varying from 0.2 to 1.5 μm was 111 μm/km at a sliding speed of 1 m/sec under a load of 0.2 MPa. This was significantly lower than the linear wear index of industrial ceramics of reaction-sintered silicon carbide (RSSC), which was 232.4 μm/km.

Pressureless Sintering and High-Temperature Strength of SiC-AlN Ceramics

High-Temperature Strength of Sic-Aln Solid-Solutions and Composites As Evaluated by Small Punch Tests

Preparation and mechanical properties of SiC-AlN ceramic alloy

High-temperature Deformation Behavior of SiC-AlN Ceramic Alloys with Fine-grained Microstructure.

Mechanical Properties of AlN-SiC Ceramic Composites Synthesized by Pressureless Sintering and Post-HIP Treatment.

Mechanical Properties of SiC-AlN Single-Phase Alloys and Two-Phase Composites.

Preparation of SiC-AlN Ceramic Alloy Powder by Direct Reaction Between Constituent Elements and Property Evaluation of Its Sintered Compacts.

PRESSURELESS SINTERING OF SILICON CARBIDE NANOCOMPOSITE CERAMICS

Pressureless Sintering of Silicon Carbide Ceramics Containing Zirconium Diboride

Pressure Sintering, Structure and Some Properties of SiC–Al Composite Materials

Low temperature fabrication of highly dense α‐Si3N4 ceramics

Effect Of Aln Content On The Pressureless Sintering Behaviors Of Sic-Aln Multiphase Ceramics

Synthesis of SiC-AlN Ceramic Alloy Powder by the Direct Reactions Between the Constituent Elements.

Sintering And Mechanical Properties Of Aln-Rich Ceramics In The Sic-Aln System

Effects of AlN Content and Sintering Atmospheres on the Thermal Conductivity of Hot-Pressed SiC Ceramics

Pressureless sintered Al4SiC4 ceramics with Y2O3 addition

Synthesis and Consolidation of Composite Materials in the SiC–Si3N4–Si2N2O System

Effects of SiC contents on the microstructure and mechanical properties of Al4SiC4–SiC ceramic composites

Carbothermally prepared nanophase SiC/ Si3N4 composite powders and densified parts

High-Temperature Properties of SiC-Si3N4 Particle Composites

Synthesis of SiC-AlN Powder and Characterization of Its HIP-Sintered Compacts.