Abstract:The influence that the atmosphere (N_2 or Ar) and sintering time have on microstructure evolution in liquid-phase-sintered alpha-sic and on its mechanical properties at high temperature was investigated. The microstructure of the samples sintered in N2 was equiaxed with a grain size of 0.70 {\mu}m and a density of 98% of the theoretical value regardless of the sintering time. In contrast, samples sintered in Ar had an elongated-grain microstructure with a density decreasing from 99% to 95% and a grain size increasing from 0.64 to 1.61 {\mu}m as the sintering time increased from 1 to 7 hours. The mechanical behaviour at 1450 °C showed the samples sintered in nitrogen to be brittle and fail at very low strains, with a fracture stress increasing from 400 to 800 MPa as the sintering time increased. In contrast, the samples sintered in Ar were quasi-ductile with increasing strain to failure as the sintering time increased, and a fracture stress strongly linked to the form and size of the grains. These differences in the mechanical properties of the two materials are discussed in the text. During mechanical tests, a loss of intergranular phase takes place in a region, between 50 and 150 {\mu}m thick, close to the surface of the samples--the effect being more important in the samples sintered in Ar

Effects of AlN Content and Sintering Atmospheres on the Thermal Conductivity of Hot-Pressed SiC Ceramics

Optimization of Microstructure to Improve Si3n4 Ceramics with Thermal Conductivity and Mechanical Properties: Effect of Si and Α-Si3n4 Powder Composition

Effect Of Aln Content On The Pressureless Sintering Behaviors Of Sic-Aln Multiphase Ceramics

Electrical properties of SiC-AlN ceramics pressureless sintered under N2 atmosphere

High infrared emissivity of SiC-AlN ceramics at room temperature

Effects of AlN and rare earth fluorides on the thermal conductivity of SiC ceramics with impedance spectroscopy analysis

Effects of Sintering Additives on the Thermoelectric Properties of SiC Ceramics

Effect of Post-Sintering Heat-Treatment on Thermal Conductivity of Si3N4 Ceramics Containing Different Additives

Pressureless Sintering and High-Temperature Strength of SiC-AlN Ceramics

The effect of aluminum additive on pressureless sintering of SiC

Effects of SiC contents on the microstructure and mechanical properties of Al4SiC4–SiC ceramic composites

Thermal conductivity and dielectric property of hot-pressing sintered AlN–BN ceramic composites

Study on Micro-structure and Properties of Al2O3/SiC Ceramics by Pressureless Sintering in Air

Microstructure and Thermal Conductivity of Spark Plasma Sintering AlN Ceramics

Effects of Li2o on the Low Temperature Sintering and Thermal Conductivity of Aln Ceramics

Thermoelectric properties of aluminum compound-doped α-SiC ceramics

Sintering of β-Si_3N_4 Powder and Thermal Conductivity of the Ceramic

Balancing thermal conductivity and strength of hot-pressed AlN ceramics via pre-sintering and annealing process

Effect of CeO2, Dy2O3, Yb 2O3 and y2O3 additives on thermal conductivity of silicon nitride ceramics

Effect of atmosphere and sintering time on the microstructure and mechanical properties at high temperatures of $α$-SiC sintered with liquid phase Y$_2$O$_3$ and Al$_2$O$_3$

High Thermal Conductivity in Pressureless Densified SiC Ceramics with Ultra-Low Contents of Additives Derived from Novel Boron–carbon Sources