Thermal conductivity and dielectric property of hot-pressing sintered AlN–BN ceramic composites

Haiyang Zhao,Weimin Wang,Zhengyi Fu,Hao Wang

DOI: https://doi.org/10.1016/j.ceramint.2007.09.111

IF: 5.532

2009-01-01

Ceramics International

Abstract:A study was conducted of the effects of sintering temperature and CaF2 additives on densification, microstructure, dielectric property and thermal conductivity of AlN–BN composites. Increasing sintering temperature and CaF2 contents help to improve the densification, thermal conductivity, and purification of the grain boundaries. Thermal conductivity value reached 110Wm−1K−1 for AlN–BN composites with 3wt.% CaF2 and sintered at 1850°C. Increasing sintering temperature decreases relative dielectric constant and tanδ. The increase in CaF2 content increases relative dielectric constant and decreases tanδ. Relative dielectric constants values were between 7.29 and 7.64 and dielectric loss tangent values ranged from 6.36 to 7.83×10−4 at 1MHz.

materials science, ceramics