Abstract:To meet the practical application, a kind of commercially available Si3N4 powder by direct Si nitridation was used to fabricate dense Si3N4/SiC nanocomposite by pressureless sintering method. The price of this kind of powder is much lower than that of powder by imide decomposition. 5-30 vol% of SiC powder (average particle size: 80 nm) were added in the composite to investigate the effect of SiC particle. Totally 15 wt% of MgAl2O4 and ZrO2 (50 wt% each) were used as sihtering additives. With increasing SiC content, the densities of the composites decreased. α-β Si3N4 phase transformation was enhanced at low temperatures, but prohibited at high temperatures for large SiC content. The sample with larger SiC content gave a relatively smaller Si3N4 grain size because SiC particles limit the Si3N4 grain growth by pinning and prohibiting the grain boundary movement. An improvement of Young's modulus, flexural strength and hardness by the SiC addition was found. Further increase in SiC content resulted in a decrease of these properties because of the decreasing density for the samples sintered at low temperatures. With an intermediate sintering temperature, the samples with 20 vol% SiC reached to high flexural strength as 1050 MPa as a result of good density and relatively fine grain size structure. The decreased fracture toughness with increasing the SiC content was observed by the refinement of Si3N4 grain. However, it was improved with the increasing sintering temperature. The result of this study provided an economic way to fabricate the Si3N4/SiC nanocomposite with a strength higher than 1 GPa and appropriate fracture toughness.

Fluoride doped SiC/Si3N4 composite as a high thermal conductive material with enhanced mechanical properties

Optimization of Microstructure to Improve Si3n4 Ceramics with Thermal Conductivity and Mechanical Properties: Effect of Si and Α-Si3n4 Powder Composition

Comparative Study of Fluoride and Non-Fluoride Additives in High Thermal Conductive Silicon Nitride Ceramics Fabricated by Spark Plasma Sintering and Post-Sintering Heat Treatment

Fabrication of Si3N4 ceramics with improved thermal conductivity by carbothermal reduction and two‐step sintering

Effect of MgF2 addition on mechanical properties and thermal conductivity of silicon nitride ceramics

Fabrication and Mechanical Properties of Si3N4/SiC Nanocompoisites under Pressureless Sintering.

Fabrication, Microstructure, and Properties of SiC/Al 4 SiC 4 Multiphase Ceramics Via an In-Situ Formed Liquid Phase Sintering

Effect of Composite Sintering Additives Containing Non-Oxide on Mechanical, Thermal and Dielectric Properties of Silicon Nitride Ceramics Substrate

Fabrication of Si 3 N 4 ceramics with high thermal conductivity and flexural strength via novel two-step gas-pressure sintering

Silicon Nitride Ceramics with High Thermal Conductivity and Excellent Mechanical Properties Fabricated with MgF2 Sintering Aid and Post Sintering Heat Treatment

Rapid Preparation of Si3N4 Ceramics with High Thermal Conductivity and Low Dielectric Loss by Fast Hot-Pressing (FHP) Sintering

Effects of AlN and rare earth fluorides on the thermal conductivity of SiC ceramics with impedance spectroscopy analysis

A high-temperature structural and wave-absorbing SiC fiber reinforced Si3N4 matrix composites

Fabrication of Si3N4 Ceramics with High Thermal Conductivity and Flexural Strength Via Novel Two-Step Gas-Pressure Sintering

Effect of Silicon Addition on Mechanical Properties of Mullite-Sic Composite Refractories

Fabrication, microstructure, and properties of SiC/Al4SiC4 multiphase ceramics via an in-situ formed liquid phase sintering

Slurry‐impregnating hot‐press sintered silicon carbide nanofiber/silicon carbide composites with Al‐B‐C as sintering additives

Fabrication and Properties of Si<sub>3</sub>N<sub>4</sub>-SiC-C Refractory Composites

Densification and Mechanical Properties of Si3N4/SiC Nanocomposite Using Si-Nitrided Si3N4 Powder

Fabrication and characterization of highly thermal conductive Si3N4/diamond composite materials

Effect of SiC on the anti-ablation resistance and flexural strength of (Hf-Ta-Zr)C-C/C composites