Abstract:With high activity h-BN powders as raw materials and without the using of any sintering additives, AlN–BN composite ceramics with 0–30 vol% were prepared by hot-pressing sintering in N2 at 1850 °C. Effect of h-BN content on the microstructure and properties of the composite ceramics was investigated. The results show that fully dense composite ceramics with h-BN content up to 20 vol% can be obtained and all composites show a fine-grain-microstructure with clean and clear boundaries. No “card room structure” of h-BN was formed in the samples. With the increasing h-BN content, the composites show a decreased bending strength, fracture toughness, Vickers hardness, thermal conductivity and dielectric constant. The application of high activity raw materials produces a significant grain-refinement strengthening effect and makes the composites exhibit a much higher strength and toughness compared with the results reported by other researchers. Due to the absence of sintering additive, the composite ceramics also show a quite low dielectric loss at both low and high frequency. An optimal comprehensive properties are obtained for the AlN-20 vol% BN composite: bending strength of 410 ± 21 MPa, fracture toughness of 4.21 ± 0.19 MPa·m1/2, Vickers hardness of 7.7 ± 0.2 GPa, thermal conductivity of 46.6 W·m−1·K−1, dielectric constant of 7.4 (1 MHz) and 7.48 (18 GHz), dielectric loss of 6.7 × 10−4 (1 MHz) and 6.18 × 10−3 (18 GHz).

Hot-pressing sintered AlN-BN ceramics with high thermal conductivity and low dielectric loss

Thermal conductivity and dielectric property of hot-pressing sintered AlN–BN ceramic composites

Effects of YH2 addition on pressureless sintered AlN ceramics

Balancing thermal conductivity and strength of hot-pressed AlN ceramics via pre-sintering and annealing process

Thermal Conductivity of AlN Ceramics Sintered with CaF2 and YF3

Preparation and properties of sintering additive-free AlN–BN composite ceramics by hot-pressing sintering

Vibration Assisted Hot‐Press Sintering of AlN Ceramics

Preparation of AlN microspheres/UHMWPE composites for insulating thermal conductors

Rapid Preparation of Si3N4 Ceramics with High Thermal Conductivity and Low Dielectric Loss by Fast Hot-Pressing (FHP) Sintering

Improvement in mechanical properties in AlN-h-BN composites with high thermal conductivity

Hot-pressing sintered BN-SiO2 composite ceramics with excellent thermal conductivity and dielectric properties for high frequency substrate

Microstructure and thermal conductivity of aluminium nitride with (CaY)F3 as the sintering aid

Effects of Y2O3 and Yttrium Aluminates As Sintering Additives on the Thermal Conductivity of AlN Ceramic Substrates

Phase composition, microstructure, electrical and thermal properties of TiN and Yb2O3-Sm2O3 doped AlN ceramics

Flexural strength, thermal and dielectric properties of AlN ceramics with BN nanoplatelets addition

Thermal Conductivity of AlN Ceramics with CaF2-YF3 Addition

Dielectric constant, dielectric loss and thermal conductivity of Si3N4 ceramics by hot pressing with CeO2–MgO as sintering aid

Dense AlN/FeSiAl composite ceramics with high thermal conductivity and strong microwave absorption

Thermal conductivities and mechanical properties of AlN ceramics fabricated by three dimensional printing

Dielectric and Microwave Absorption Properties of AlN‐SiBCN Lossy Ceramics

Effect of YF3 on densification behavior and thermal conductivity of AlN ceramics with Y2O3–YF3 additives under reducing atmosphere