Abstract:The AlN/BN composite ceramic, fabricated via hot-press sintering, exhibits obvious anisotropy due to the establishment of directional alignment of h-BN. However, the variation and influence mechanisms of bending strength (σ) and thermal conductivity (λ) are remain unclear in different directions, which greatly limit the application of AlN/BN composite ceramics. In this paper, the effects of h-BN content on phase composition, microstructure and anisotropy of AlN/BN composite ceramics are discussed in detail. The results reveal that AlN/BN composite ceramics have three directions: perpendicular (⊥), longitudinal parallel (∥), and lateral parallel (≡) to the hot-pressing direction. The content of h-BN is a crucial factor affecting the anisotropy of AlN/BN composite ceramics. h-BN enhances the thermal conductivity in the ∥ and hinders the thermal conductivity in the ⊥. With the increase in h-BN amount, λ∥ rises gradually, while λ⊥ gradually falls. When the mass percentage of h-BN and AlN is 25 % (AB25), the λ∥ is as high as 90 W m−1 K−1, which is about 2.25 times that of λ⊥. In terms of mechanical properties, σ ≡ and σ ⊥ first increase and then decrease, while σ ∥ only decreases. This is attributable to h-BN being effective in enhancing mechanical properties by inhibiting crack propagation in the ⊥ and ≡ direction, while the promotion of crack propagation leads to a decrease in mechanical properties in the ∥ direction. σ ≡ reaches the highest values (σ ≡ = 460.2 MPa) at an h-BN amount of 10 % (AB10), which is about 1.19 and 2.04 times that of σ ⊥ and σ ∥, respectively, and 22.1 % higher than that of AB0.

Flexural strength, thermal and dielectric properties of AlN ceramics with BN nanoplatelets addition

Improving Thermal Conductivity of Epoxy Resin by Filling Boron Nitride Nanomaterials: A Molecular Dynamics Investigation

Improvement in mechanical properties in AlN-h-BN composites with high thermal conductivity

Enhanced thermal shock resistance of BN-based composites sintered by hot-pressing with the introduction of nano oxides

Effect of hexagonal boron nitride content on the anisotropy of hot-press-sintered AlN/BN composite ceramics

Preparation and properties of sintering additive-free AlN–BN composite ceramics by hot-pressing sintering

Effect of Boron Nitride Addition on Densification, Microstructure, Mechanical, Thermal, and Dielectric Properties of β-SiAlON Ceramic

Hot-pressing sintered AlN-BN ceramics with high thermal conductivity and low dielectric loss

Fabrication and thermal conductivity of AlN/BN ceramics by spark plasma sintering

Enhanced piezoelectric and mechanical properties of AlN-modified BaTiO3 composite ceramics

Microstructure and mechanical properties of AlN–hBN based machinable ceramics prepared by pressureless sintering

Fabrication and Mechanical Properties of Boron Nitride Nanotube Reinforced Silicon Nitride Ceramics

Effects of Additive to Bn Interlayers on Microstructure and Properties of Laminated Si3n4/Bn Ceramics

Effects of YH2 addition on pressureless sintered AlN ceramics

Phase composition, microstructure, electrical and thermal properties of TiN and Yb2O3-Sm2O3 doped AlN ceramics

Synergetic enhancement of thermal conductivity by constructing BN and AlN hybrid network in epoxy matrix

Effect of AlN Addition on Phase Formation in the LTCC with Al2O3/AlN Biphasic Ceramics Based on BBSZ Glass

Densification and comprehensive properties of h-BN-based refractories with in-situ formation of Y3Al5O12

Mechanical and thermal properties of in situ AlN/Al-12Si composite fabricated by laser powder bed fusion

Effect of AlN nanoparticle doping on thermophysical properties of nitrate via mechanical milling: Experimental studies and microscopic mechanisms

Microstructure and thermal conductivity of AlN ceramics with ultra-fine Y2O3 powder addition