Abstract:With high activity h-BN powders as raw materials and without the using of any sintering additives, AlN–BN composite ceramics with 0–30 vol% were prepared by hot-pressing sintering in N2 at 1850 °C. Effect of h-BN content on the microstructure and properties of the composite ceramics was investigated. The results show that fully dense composite ceramics with h-BN content up to 20 vol% can be obtained and all composites show a fine-grain-microstructure with clean and clear boundaries. No “card room structure” of h-BN was formed in the samples. With the increasing h-BN content, the composites show a decreased bending strength, fracture toughness, Vickers hardness, thermal conductivity and dielectric constant. The application of high activity raw materials produces a significant grain-refinement strengthening effect and makes the composites exhibit a much higher strength and toughness compared with the results reported by other researchers. Due to the absence of sintering additive, the composite ceramics also show a quite low dielectric loss at both low and high frequency. An optimal comprehensive properties are obtained for the AlN-20 vol% BN composite: bending strength of 410 ± 21 MPa, fracture toughness of 4.21 ± 0.19 MPa·m1/2, Vickers hardness of 7.7 ± 0.2 GPa, thermal conductivity of 46.6 W·m−1·K−1, dielectric constant of 7.4 (1 MHz) and 7.48 (18 GHz), dielectric loss of 6.7 × 10−4 (1 MHz) and 6.18 × 10−3 (18 GHz).

Microstructure and mechanical properties of AlN–hBN based machinable ceramics prepared by pressureless sintering

High pressure sintering behavior and mechanical properties of cBN-Ti 3Al and cBN-Ti 3Al-Al composite materials

Analysis of Mechanical Properties of Al2O3‐cBN‐hBN Composites and Identification of Main Influencing Factors

Study of machinable AlN/BN ceramic composites

Fabrication of machinable AlN–BN composites with high thermal conductivity by pressureless sintering turbostatic BN-coated AlN nanocomposite powders

Preparation and properties of sintering additive-free AlN–BN composite ceramics by hot-pressing sintering

High-pressure synthesis of Al<sub>2</sub>O<sub>3</sub>-cBN composites: Effect of thermodynamic condition and cBN volume fraction on their microstructure and properties

Machinable Al2O3/BN Composite Ceramics with Strong Mechanical Properties

Fabrication and Properties of Machinable AlN-BN Ceramic Nanocomposites

Addition of h-BN for enhanced machinability and high mechanical strength of AlN/Mo composites

Effect of impregnating and heat treatment on microstructure and properties of pressureless sintering AlN/h-BN composite ceramics

Fabrication of Machinable BN/Al2O3 Ceramic Composites

Effects of Weak Boundary Phases (WBP) on the Microstructure and Mechanical Properties of Pressureless Sintered Al2O3/h-BN Machinable Composites

Effects of AlN Content on Phase Composition, Microstructure and Mechanical Properties of BN-based Composite Ceramics

Investigation of mechanical property and thermal shock behavior of machinable B4C/BN ceramics composites

Effects of AlN content on phase composition, microstructure and mechanical properties of DN-based composite ceramics

Machinability, deformation, and cracks behavior of pressureless-sintered Al2O3/h-BN composites: role of weak boundary phases

Improvement in mechanical properties in AlN-h-BN composites with high thermal conductivity

Fabrication and properties of the machinable B4C/BN composites ceramics

Investigation on the preparation and machinability of the B4C/BN nanocomposites by hot-pressing process