Influence of hot-press sintering parameters on microstructures and mechanical properties of h-BN ceramics

Xiaoming Duan,Dechang Jia,Zheng Wang,Delong Cai,Zhuo Tian,Zhihua Yang,Peigang He,Shengjin Wang,Yu Zhou

DOI: https://doi.org/10.1016/j.jallcom.2016.05.153

IF: 6.2

2016-11-01

Journal of Alloys and Compounds

Abstract:Pure h-BN ceramics were processed at different sintering temperatures and hold times using ball milled nanocrystalline or amorphous h-BN powders. Increases in sintering temperature induced greater grain growth but reduced relative densities and mechanical properties. Changes in sintering hold times caused further increases in grain sizes and relative density, but had little impact on mechanical properties. The grain sizes play an important aspect of strength in h-BN ceramics. The relationship of flexural strength and grain sizes in h-BN ceramics conforms to Hall-Petch behavior. When the grain size of h-BN ceramics increased from 0.3 μm to 8 μm, the flexural strength declined from 163 ± 6 to 84 ± 4 MPa. The mechanical properties of h-BN ceramics depend both on relative densities and grain sizes.

materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering