Abstract:The AlN/BN composite ceramic, fabricated via hot-press sintering, exhibits obvious anisotropy due to the establishment of directional alignment of h-BN. However, the variation and influence mechanisms of bending strength (σ) and thermal conductivity (λ) are remain unclear in different directions, which greatly limit the application of AlN/BN composite ceramics. In this paper, the effects of h-BN content on phase composition, microstructure and anisotropy of AlN/BN composite ceramics are discussed in detail. The results reveal that AlN/BN composite ceramics have three directions: perpendicular (⊥), longitudinal parallel (∥), and lateral parallel (≡) to the hot-pressing direction. The content of h-BN is a crucial factor affecting the anisotropy of AlN/BN composite ceramics. h-BN enhances the thermal conductivity in the ∥ and hinders the thermal conductivity in the ⊥. With the increase in h-BN amount, λ∥ rises gradually, while λ⊥ gradually falls. When the mass percentage of h-BN and AlN is 25 % (AB25), the λ∥ is as high as 90 W m−1 K−1, which is about 2.25 times that of λ⊥. In terms of mechanical properties, σ ≡ and σ ⊥ first increase and then decrease, while σ ∥ only decreases. This is attributable to h-BN being effective in enhancing mechanical properties by inhibiting crack propagation in the ⊥ and ≡ direction, while the promotion of crack propagation leads to a decrease in mechanical properties in the ∥ direction. σ ≡ reaches the highest values (σ ≡ = 460.2 MPa) at an h-BN amount of 10 % (AB10), which is about 1.19 and 2.04 times that of σ ⊥ and σ ∥, respectively, and 22.1 % higher than that of AB0.

Influence of sintering temperature on the crystallization and mechanical properties of BN‐MAS composites

Influence of sintering pressure on the crystallization and mechanical properties of BN-MAS composite ceramics

Effects of sintering temperature on the microstructure and properties of h-BN ceramics with MAS as liquid sintering aid

High pressure sintering behavior and mechanical properties of cBN-Ti 3Al and cBN-Ti 3Al-Al composite materials

Effect of sintering temperature on microstructure and mechanical properties of boron nitride whisker reinforced fused silica composites

Anisotropies in structure and properties of hot-press sintered h-BN-MAS composite ceramics: Effects of raw h-BN particle size

Enhanced thermal shock resistance of BN-based composites sintered by hot-pressing with the introduction of nano oxides

Microstructural evolution of h-BN matrix composite ceramics with La-Al-Si-O glass phase during hot-pressed sintering

Hot-press sintering studies of sol-gel-prepared composite powders: A novel preparation method to improve mechanical properties of BN-BAS composite ceramics

Influence of hot-press sintering parameters on microstructures and mechanical properties of h-BN ceramics

Analysis of Mechanical Properties of Al2O3‐cBN‐hBN Composites and Identification of Main Influencing Factors

Fabrication of High Strength α-SiAlON/BN Composition Ceramics by Hot Pressing

High-pressure Synthesis of Al2O3-cBN Composites: Effect of Thermodynamic Condition and Cbn Volume Fraction on Their Microstructure and Properties

Microstructure and room/elevated-temperature mechanical properties of hot-pressed h-BN composite ceramics with La2O3-Al2O3-SiO2 addition

Microstructures and mechanical properties of B4C‐SiC and B4C‐SiC‐TiB2 ceramic composites fabricated by hot pressing

Effect of hexagonal boron nitride content on the anisotropy of hot-press-sintered AlN/BN composite ceramics

Effect of sintering temperature and holding time on the microstructure and mechanical properties of ZrB2–SiCw composites

Beneficial effect of low BN additive on densification and mechanical properties of hot-pressed ZrB2–SiC composites

Improvement in mechanical properties in AlN-h-BN composites with high thermal conductivity

Microstructure and Mechanical Properties of ZrB2/h-BN Multiphase Ceramics by Low-Temperature Reactive Sintering