Abstract:Dense polycrystalline cubic boron nitride (PcBN) composites were fabricated by high-pressure and high-temperature (HPHT) sintering using polysilazane (PSN) and Al as sintering additive. After high-energy ball milling, the cBN fine particles were uniformly coated with PSN by ultrasonic treatment. After thermocuring and pyrolysis, the cBN–SiCN particles were mixed with Al. The PcBN composites were prepared after sintering at 1450 °C for 10 min with a pressure of 5 GPa. The refining effect of high-energy ball milling on the cBN particles was studied by scanning electron microscopy (SEM) and laser particle size analyzer. The oxidation of the cBN particles after milling was investigated by nitrogen–oxygen analyzer. The phase composition and microstructure of the sintered PcBN composites were investigated by X-ray diffractometer (XRD) and SEM. The main phases of the sintered PcBN composites are cBN, AlN, SiC and Si3N4. The conversion of cBN to hBN was inhibited by the formation of AlN. The mechanical properties of the sintered PcBN composites were improved by the appearance of SiC and Si3N4. The density and mechanical properties of the PcBN composites both increased with the content of the cBN particles increasing. The sintered sample with 60 wt% cBN, 30 wt% PSN and 10 wt% Al showed the best results: density of 99.7%, Vickers' hardness of (25.2 ± 0.8) GPa and flexural strength of (602 ± 15) MPa.<h3 class="a-plus-plus">Graphic abstract</h3>

High-pressure synthesis of Al<sub>2</sub>O<sub>3</sub>-cBN composites: Effect of thermodynamic condition and cBN volume fraction on their microstructure and properties

High pressure sintering behavior and mechanical properties of cBN-Ti 3Al and cBN-Ti 3Al-Al composite materials

High-pressure Synthesis of Tungsten Carbide–cubic Boron Nitride (wc–cbn) Composites: Effect of Cbn Particle Size and Volume Fraction on Their Microstructure and Properties

Analysis of Mechanical Properties of Al2O3‐cBN‐hBN Composites and Identification of Main Influencing Factors

Synthesis and characterization of cubic boron nitride (Al)-Al2O3 composites under high pressure and high temperature conditions

Study of High-Pressure Sintering Behavior of Cbn Composites Starting with Cbn–al Mixtures

High Pressure Synthesis of Tungsten Carbide–Cubic Boron Nitride (WC–cBN) Composites: Effect of Thermodynamic Condition and cBN Volume Fraction on their Microstructure and Properties

In situ high pressure synthesis of cBN-based composites

Enhanced thermal shock resistance of BN-based composites sintered by hot-pressing with the introduction of nano oxides

High-Pressure synthesis of Al2O3-cBN-hBN Self-lubricating ceramic

Hard and tough ultrafine-grained B4C-cBN composites prepared by high-pressure sintering

Sound velocities, elasticity and thermal properties of cBN composite with AlN binder at high pressure

Phase composition, microstructure, and mechanical properties of PcBN composites with Ti and Ti Al binders: Effects of holding time and synthesis pressure

Cbn-Al2o3 Composites in NaCl Environment under High Pressure and High Temperature Conditions

Effects of TiAl Alloy as a Binder on Cubic Boron Nitride Composites

High Pressure and High Temperature Sintered PcBN Using Al, B4C and C as Sintering Additive

Synthesis and Characterization of Novel Ti3SiC2–cBN Composites

Processing and properties of PcBN composites fabricated by HPHT using PSN and Al as sintering additive

Synthesis and Performance Study of Polycrystalline Cubic Boron Nitride Using WC–B4C–Al2O3 as a Binder

Densification and mechanical properties of boron carbide prepared via spark plasma sintering with cubic boron nitride as an additive

Spark plasma sintering of cBN/β-SiAlON composites