Microstructure and mechanical properties of h-BN–SiC ceramic composites prepared by in situ combustion synthesis

Y.T. Zheng,H.B. Li,T. Zhou

DOI: https://doi.org/10.1016/j.msea.2012.01.105

2012-04-01

Abstract:h-BN–SiC ceramic composites were prepared by in situ combustion synthesis of B4C and Si powder compacts under high nitrogen pressure. The high reaction nitrogen pressure was beneficial to the improvement of the relative density and mechanical properties of the products, but higher nitrogen pressure of 120MPa was favorable to the formation of Si3N4, which was consistent with the theoretical thermodynamic calculation. The h-BN–SiC ceramic composites have good mechanical properties over those of conventionally processed ones because of the in situ formed h-BN and SiC phases fabricated under high temperature and pressure. The bending strength and fracture toughness of the h-BN–SiC ceramic composites prepared under 100MPa nitrogen pressure were 82MPa and 1.9MPam1/2, respectively.