Abstract:Cubic boron nitride (cBN) with high hardness, thermal conductivity, wear resistance, and chemical inertness has become the most promising abrasive and machining material. Due to the difficulty of fabricating pure cBN body, generally, some binders are incorporated among cBN particles to prepare polycrystalline cubic boron nitride (PcBN). Hence, the binders play a critical factor to the performances of PcBN composites. In this study, the PcBN composites with three binder systems containing ceramic and metal phases were fabricated by spark plasma sintering (SPS) from 1400 to 1700 °C. The sintering behaviors and mechanical properties of the composites were investigated. Results show that the effect of binder formulas on mechanical properties mainly related to the compactness, mechanical performances, and thermal expansion coefficient of binder phases, which affect the carrying capacity of the composites and the bonding strength between binder phases and cBN particles. The PcBN composite with SiAlON phase as binder presented optimal flexural strength (465±29 MPa) and fracture toughness (5.62±0.37 MPa·m 1/2 ), attributing to the synergistic effect similar to transgranular and intergranular fractures. Meanwhile, the excellent mechanical properties can be maintained a comparable level when the temperature even rises to 800 °C. Due to the weak bonding strength and high porosity, the PcBN composites with Al 2 O 3 -ZrO 2 (3Y) and Al-Ti binder systems exhibited inferior mechanical properties. The possible mechanisms to explain these results were also analyzed.

Phase composition, microstructure, and mechanical properties of PcBN composites with Ti and Ti Al binders: Effects of holding time and synthesis pressure

High pressure sintering behavior and mechanical properties of cBN-Ti 3Al and cBN-Ti 3Al-Al composite materials

High-pressure synthesis of Al<sub>2</sub>O<sub>3</sub>-cBN composites: Effect of thermodynamic condition and cBN volume fraction on their microstructure and properties

Effect of TiB_2 content on microstructure and mechanical properties of in-situ fabricated TiB_2/B_4C composites

Effect of Al Ti content on mechanical properties of in-situ synthesized PcBN composites

High-pressure Synthesis of Tungsten Carbide–cubic Boron Nitride (wc–cbn) Composites: Effect of Cbn Particle Size and Volume Fraction on Their Microstructure and Properties

In situ synthesis of PcBN composites by Sialon combined with cBN-TiB2-AlN and their properties

Effects of TiAl Alloy as a Binder on Cubic Boron Nitride Composites

Synthesis and characterization of cubic boron nitride (Al)-Al2O3 composites under high pressure and high temperature conditions

Analysis of Mechanical Properties of Al2O3‐cBN‐hBN Composites and Identification of Main Influencing Factors

Effect of Y2O3 additive on properties of PCBN composites with TiN-Ti-AlN as binder by high temperature and high pressure sintering

High Pressure and High Temperature Sintered PcBN Using Al, B4C and C as Sintering Additive

Influence of Sintering Temperature on Structure and Mechanical Properties of Polycrystalline Cubic Boron Nitride Composites

Hard and tough ultrafine-grained B4C-cBN composites prepared by high-pressure sintering

Influence of binder systems on sintering characteristics, microstructures, and mechanical properties of PcBN composites fabricated by SPS

Enhanced thermal shock resistance of BN-based composites sintered by hot-pressing with the introduction of nano oxides

Synthesis and Characterization of Novel Ti3SiC2–cBN Composites

High Pressure Synthesis of Tungsten Carbide–Cubic Boron Nitride (WC–cBN) Composites: Effect of Thermodynamic Condition and cBN Volume Fraction on their Microstructure and Properties

Synthesis and Mechanical Properties of TiB2/Ti2AlN Composites Fabricated by Hot Pressing Sintering

Microstructure and Performance of Solidified TiB2TiC Composites Prepared by High Pressure and High Temperature

Synthesis and Performance of TiB2–B4C Composites by High Pressure of TiC–B Mixture