Abstract:To reduce the negative effects of the long-time and B2O3 phase on the traditional sintering process for B4C-based composite ceramics, nearly fully dense B4C–VB2 composite ceramics were prepared by reactive spark plasma sintering (SPS) technology at 2000 °C with B and V8C7 powders as raw materials in this paper. The effects of the degassing time during SPS on the microstructure and the mechanical properties of the final products were investigated in detail. The results revealed that the proper degassing time was beneficial for the vent of B2O3 during the sintering process, which refined the grain size, promoted densification and improved the mechanical properties of the composite ceramic. However, the redundant degassing time increased the holding time at high temperature, resulting in abnormal grain growth and mechanical performance deterioration. In the present work, the optimal degassing time was 6 min, and the final product prepared under the above conditions exhibited excellent comprehensive performance with a relative density of 99.2%, Vickers hardness of 31.2 GPa, bending strength of 654 MPa and fracture toughness of 5.7 MPa m1/2. In addition, the strengthening and toughening mechanisms of the products were mainly attributed to the residual thermal stresses and bridging structure caused by the fine B4C and VB2 grains distributed uniformly.

Densification and mechanical properties of boron carbide prepared via spark plasma sintering with cubic boron nitride as an additive

Effect of TiB_2 content on microstructure and mechanical properties of in-situ fabricated TiB_2/B_4C composites

High-pressure synthesis of Al<sub>2</sub>O<sub>3</sub>-cBN composites: Effect of thermodynamic condition and cBN volume fraction on their microstructure and properties

Hard and tough ultrafine-grained B4C-cBN composites prepared by high-pressure sintering

High-pressure Synthesis of Tungsten Carbide–cubic Boron Nitride (wc–cbn) Composites: Effect of Cbn Particle Size and Volume Fraction on Their Microstructure and Properties

Influence of Length-Scale on Stabilization of Boron Carbide in Al-based Metal Matrix Composites During Plasma Activated Sintering

In situ synthesis of PcBN composites by Sialon combined with cBN-TiB2-AlN and their properties

Synthesis of cBN-hBN-SiCw Nanocomposite with Superior Hardness, Strength, and Toughness

Enhanced thermal shock resistance of BN-based composites sintered by hot-pressing with the introduction of nano oxides

Preparation of superhard cubic boron nitride sintered from commercially available submicron powders

Multi-stage spark plasma sintering to study the densification mechanisms of boron carbide

Analysis of Mechanical Properties of Al2O3‐cBN‐hBN Composites and Identification of Main Influencing Factors

The Effect of CNTs on the Spark Plasma Sintering Densification Behavior and Mechanical Properties of B4C-Si Powders

Fabrication and characterization of hot-pressed B-rich boron carbide

Microstructure, mechanical properties and thermal shock behavior of h-BN-SiC ceramic composites prepared by spark plasma sintering

Enhancement mechanical properties of in-situ preparated B4C-based composites with small amount of (Ti3SiC2+Si)

Beneficial effect of low BN additive on densification and mechanical properties of hot-pressed ZrB2–SiC composites

Preparation and mechanical properties of laminated B4C–TiB2/BN ceramics

Densification and strengthening mechanism in spark plasma sintering of B4C–VB2 ceramics via carbide boronizing

Microstructure and Mechanical Properties of Ultrafine WC–Ni–VC–TaC–cBN Cemented Carbides Fabricated by Spark Plasma Sintering