Abstract:SiC/h-BN multiphase ceramics were prepared via spark plasma sintering (SPS) with t-BN and SiC nanopowders as raw materials and B2O3 as a sintering additive. The phase composition and microstructure of specimens were characterized by X-ray diffraction and scanning electronic microscopy. The effect of sintering additive content on the sintering behavior, densification, microstructure and mechanical properties of SiC/h-BN multiphase ceramics was investigated. The results show that the addition of B2O3 can effectively increase the density and mechanical properties at a low sintering temperature. Compared to the samples without B2O3 additive, the B2O3 additive is effective to decrease the initial shrinkage temperature, promote the rearrangement of h-BN flake grains and improve the bonding strength between the grains. The density of multiphase ceramics increases, and the mechanical properties firstly increase and then decrease with the increase of sintering additive content. The relative density and mechanical properties of the sample with 5% B2O3 content are better than those of other samples, and the relative density, flexural strength, fracture toughness and elastic modulus are 96.92%, 274.7 MPa, 2.91 MPa·m1/2 and 127.2 GPa, respectively. However, the excessive addition of B2O3 is not conducive to the improvement of mechanical properties.

Effects of h-BN addition on microstructures and mechanical properties of β-CaSiO3 bioceramics

Effect of Hexagonal BN on the Microstructure and Mechanical Properties of Pressureless Sintered Porous Si3N4 Ceramics

Microstructure and room/elevated-temperature mechanical properties of hot-pressed h-BN composite ceramics with La2O3-Al2O3-SiO2 addition

Effect of h-BN on the mechanical and dielectric properties of porous h-BN/Si3N4 composite ceramics prepared by gel casting

Effect of B2O3 Addition on Low-temperature Sintering Behavior and Properties of SiC/h-BN Multiphase Ceramics

Effects of Additive to Bn Interlayers on Microstructure and Properties of Laminated Si3n4/Bn Ceramics

Effect Of H-Bn Content On The Sintering Properties Of Sic-Yag-Bn Multiphase Ceramics

Effects of h‐BN on the thermal shock and oxidation resistance of SiO2‐bonded SiC refractories

Effects of BN on the microstructural evolution and mechanical properties of BAS-BN composites

Influence of hot-press sintering parameters on microstructures and mechanical properties of h-BN ceramics

Fabrication and Properties of Pressureless Sintered Si3N4/BN Composite Ceramics with La2O3-Al2O3-Y2O3 as Sintering Additives

Mechanical and wear properties of h-BN/Si3N4 ceramic composites

Microstructural evolution of h-BN matrix composite ceramics with La-Al-Si-O glass phase during hot-pressed sintering

Effects of H-Bn on Mechanical Properties of Reaction Bonded Β-Sialon/h-bn Composites

Microstructural Evolution of H-BN Matrix Composite Ceramics With Amorphous La2O3-Al2O3-SiO2 Glass Phase During Hot Pressing

The Study on the Property and the Microstructure of Pressureless Sintered h-BN Ceramics

Fabrication of High Strength α-SiAlON/BN Composition Ceramics by Hot Pressing

Improved thermal shock and oxidation resistance of β-SiAlON incorporated with h-BN

Effect of Nano SiC on Microstructure and Mechanical Properties of BN-ZrO2-SiC Multiphase Ceramics

Fabrication and properties of Si3N4/BN composite ceramics by pressureless sintering with Yb2O3-Al 2O3-Y2O3 as sintering additives