Effect of B2O3 Addition on Low-temperature Sintering Behavior and Properties of SiC/h-BN Multiphase Ceramics

Fengrui ZHAI,Shuang LI,Zhipeng XIE,Jialin SUN,Zhongzhou YI

DOI: https://doi.org/10.14062/j.issn.0454-5648.2016.03.01

2016-01-01

Abstract:SiC/h-BN multiphase ceramics were prepared via spark plasma sintering (SPS) with t-BN and SiC nanopowders as raw materials and B2O3 as a sintering additive. The phase composition and microstructure of specimens were characterized by X-ray diffraction and scanning electronic microscopy. The effect of sintering additive content on the sintering behavior, densification, microstructure and mechanical properties of SiC/h-BN multiphase ceramics was investigated. The results show that the addition of B2O3 can effectively increase the density and mechanical properties at a low sintering temperature. Compared to the samples without B2O3 additive, the B2O3 additive is effective to decrease the initial shrinkage temperature, promote the rearrangement of h-BN flake grains and improve the bonding strength between the grains. The density of multiphase ceramics increases, and the mechanical properties firstly increase and then decrease with the increase of sintering additive content. The relative density and mechanical properties of the sample with 5% B2O3 content are better than those of other samples, and the relative density, flexural strength, fracture toughness and elastic modulus are 96.92%, 274.7 MPa, 2.91 MPa·m1/2 and 127.2 GPa, respectively. However, the excessive addition of B2O3 is not conducive to the improvement of mechanical properties.