Abstract:The AlN/BN composite ceramic, fabricated via hot-press sintering, exhibits obvious anisotropy due to the establishment of directional alignment of h-BN. However, the variation and influence mechanisms of bending strength (σ) and thermal conductivity (λ) are remain unclear in different directions, which greatly limit the application of AlN/BN composite ceramics. In this paper, the effects of h-BN content on phase composition, microstructure and anisotropy of AlN/BN composite ceramics are discussed in detail. The results reveal that AlN/BN composite ceramics have three directions: perpendicular (⊥), longitudinal parallel (∥), and lateral parallel (≡) to the hot-pressing direction. The content of h-BN is a crucial factor affecting the anisotropy of AlN/BN composite ceramics. h-BN enhances the thermal conductivity in the ∥ and hinders the thermal conductivity in the ⊥. With the increase in h-BN amount, λ∥ rises gradually, while λ⊥ gradually falls. When the mass percentage of h-BN and AlN is 25 % (AB25), the λ∥ is as high as 90 W m−1 K−1, which is about 2.25 times that of λ⊥. In terms of mechanical properties, σ ≡ and σ ⊥ first increase and then decrease, while σ ∥ only decreases. This is attributable to h-BN being effective in enhancing mechanical properties by inhibiting crack propagation in the ⊥ and ≡ direction, while the promotion of crack propagation leads to a decrease in mechanical properties in the ∥ direction. σ ≡ reaches the highest values (σ ≡ = 460.2 MPa) at an h-BN amount of 10 % (AB10), which is about 1.19 and 2.04 times that of σ ⊥ and σ ∥, respectively, and 22.1 % higher than that of AB0.

Effect of sintering pressure on the texture of hot-press sintered hexagonal boron nitride composite ceramics

High pressure sintering behavior and mechanical properties of cBN-Ti 3Al and cBN-Ti 3Al-Al composite materials

Influence of sintering pressure on the crystallization and mechanical properties of BN-MAS composite ceramics

Anisotropic mechanical properties and fracture mechanisms of textured h-BN composite ceramics

Effect of Hexagonal BN on the Microstructure and Mechanical Properties of Pressureless Sintered Porous Si3N4 Ceramics

Texture and anisotropy of hot-pressed h-BN matrix composite ceramics with in situ formed YAG

The effects of holding time on grain size, orientation degree and properties of h-BN matrix textured ceramics

High-pressure Synthesis of Tungsten Carbide–cubic Boron Nitride (wc–cbn) Composites: Effect of Cbn Particle Size and Volume Fraction on Their Microstructure and Properties

Ion sputtering erosion mechanisms of h-BN composite ceramics with textured microstructures

Influence of hot-press sintering parameters on microstructures and mechanical properties of h-BN ceramics

Analysis of Mechanical Properties of Al2O3‐cBN‐hBN Composites and Identification of Main Influencing Factors

The Study on the Property and the Microstructure of Pressureless Sintered h-BN Ceramics

Anisotropic properties of textured h-BN matrix ceramics prepared using 3Y2O3-5Al2O3(-4MgO) as sintering additives

High-pressure synthesis of Al<sub>2</sub>O<sub>3</sub>-cBN composites: Effect of thermodynamic condition and cBN volume fraction on their microstructure and properties

Preparation of h-BN-Based Textured Ceramics by Grain Rearrangement During Ultraviolet Curing Assisted Hot-Press Sintering

Influence of sintering temperature on the crystallization and mechanical properties of BN‐MAS composites

Effect of Pressure During Hot-pressing on Microstructure and Mechanical Properties of B/Al Composite

Anisotropies in structure and properties of hot-press sintered h-BN-MAS composite ceramics: Effects of raw h-BN particle size

Effect of hexagonal boron nitride content on the anisotropy of hot-press-sintered AlN/BN composite ceramics