Abstract:The AlN/BN composite ceramic, fabricated via hot-press sintering, exhibits obvious anisotropy due to the establishment of directional alignment of h-BN. However, the variation and influence mechanisms of bending strength (σ) and thermal conductivity (λ) are remain unclear in different directions, which greatly limit the application of AlN/BN composite ceramics. In this paper, the effects of h-BN content on phase composition, microstructure and anisotropy of AlN/BN composite ceramics are discussed in detail. The results reveal that AlN/BN composite ceramics have three directions: perpendicular (⊥), longitudinal parallel (∥), and lateral parallel (≡) to the hot-pressing direction. The content of h-BN is a crucial factor affecting the anisotropy of AlN/BN composite ceramics. h-BN enhances the thermal conductivity in the ∥ and hinders the thermal conductivity in the ⊥. With the increase in h-BN amount, λ∥ rises gradually, while λ⊥ gradually falls. When the mass percentage of h-BN and AlN is 25 % (AB25), the λ∥ is as high as 90 W m−1 K−1, which is about 2.25 times that of λ⊥. In terms of mechanical properties, σ ≡ and σ ⊥ first increase and then decrease, while σ ∥ only decreases. This is attributable to h-BN being effective in enhancing mechanical properties by inhibiting crack propagation in the ⊥ and ≡ direction, while the promotion of crack propagation leads to a decrease in mechanical properties in the ∥ direction. σ ≡ reaches the highest values (σ ≡ = 460.2 MPa) at an h-BN amount of 10 % (AB10), which is about 1.19 and 2.04 times that of σ ⊥ and σ ∥, respectively, and 22.1 % higher than that of AB0.

Texture and anisotropy of hot-pressed h-BN matrix composite ceramics with in situ formed YAG

Anisotropic properties of textured h-BN matrix ceramics prepared using 3Y2O3-5Al2O3(-4MgO) as sintering additives

Preparation of h-BN-Based Textured Ceramics by Grain Rearrangement During Ultraviolet Curing Assisted Hot-Press Sintering

Anisotropic mechanical properties and fracture mechanisms of textured h-BN composite ceramics

Preparation of highly oriented h-BN based textured ceramics via grain rearrangement under DLP printing and low-pressure sintering

Microstructural Evolution and Mechanical Properties of H-Bn Composite Ceramics with Y 2 O 3 –aln Addition by Liquid-Phase Sintering

Microstructural evolution and mechanical properties of h-BN composite ceramics with Y2O3–AlN addition by liquid-phase sintering

Microstructure of hot-pressed h-BN/Si3N4 ceramic composites with Y2O3–Al2O3 sintering additive

The effects of holding time on grain size, orientation degree and properties of h-BN matrix textured ceramics

Effect of sintering pressure on the texture of hot-press sintered hexagonal boron nitride composite ceramics

Anisotropies in structure and properties of hot-press sintered h-BN-MAS composite ceramics: Effects of raw h-BN particle size

Microstructure and room/elevated-temperature mechanical properties of hot-pressed h-BN composite ceramics with La2O3-Al2O3-SiO2 addition

Effect of hexagonal boron nitride content on the anisotropy of hot-press-sintered AlN/BN composite ceramics

Microstructural Evolution of H-BN&nbsp;Matrix Composite Ceramics With Amorphous La2O3-Al2O3-SiO2&nbsp;Glass Phase During Hot Pressing

Microstructural Evolution of H-BN Matrix Composite Ceramics With Amorphous La2O3-Al2O3-SiO2 Glass Phase During Hot Pressing

High-pressure synthesis of Al<sub>2</sub>O<sub>3</sub>-cBN composites: Effect of thermodynamic condition and cBN volume fraction on their microstructure and properties

Microstructural evolution of h-BN matrix composite ceramics with La-Al-Si-O glass phase during hot-pressed sintering

Fabrication of High Strength α-SiAlON/BN Composition Ceramics by Hot Pressing

Enhanced thermal shock resistance of BN-based composites sintered by hot-pressing with the introduction of nano oxides