Abstract:The non-oxide-reinforced phase AlN-SiC solid solution with high performance was successfully synthesized in the resin-bonded Al-Si-SiC composites under flowing nitrogen at 1300 °C. The AlN-SiC solid solution was synthesized by three paths of liquid-solid, gas-solid and gas-gas reactions through modulation of Al/Si ratio, and controllable microstructure of AlN-SiC solid solution was attained. The phase composition and microstructure of the sintered samples were characterized by XRD and SEM, combined with thermodynamics, the formation mechanism of AlN-SiC solid solution was investigated and the reaction model was established. Al was not detected while Si was detested by XRD. Granular, short columnar and whisker-like AlN-SiC solid solution were generated and their positions varied. As the temperature increases, the partial pressure of oxygen decreases due to the oxidation of Al, Si and SiC on the surface of the sample, inside the sample, the active oxidation takes place, generating Al2O(g), SiO(g) and CO(g). Due to the low oxygen partial pressure, Al is preferentially nitrided to form a thin AlN layer on its surface. The AlN layer is broken as the temperature increases, then liquid Al with carbon from resin begins to flow, leaving the residual shell of AlN in situ. When it flows to the surface of Si, Al-Sialloy is formed locally inside the Si particles under the wetting effect of C, then hexagonal AlN-SiC solid solution is formed inside the Si shell. Part of SiO(g) + CO(g) diffuses into the interior of the AlN residual shell and reacts by aggregation to form a granular AlN-SiC solid solution in the shell wall; others diffuses into the pores of the sample for vapor deposition, and finally forms stacked hexagonal flaky whiskers. The in-situ generated of AlN-SiC solid solution with multiple morphologies in the composite plays a joint toughening effect, which can significantly enhance the comprehensive performance of the composite. In this experiment, the synthesis of AlN-SiC solid solution without sintering aids under normal pressure at a low temperature. It is expected to be applied to the blast furnace and to realize the longevity of blast furnace.

Mechanical Properties of SiC-AlN Single-Phase Alloys and Two-Phase Composites.

Preparation and mechanical properties of SiC-AlN ceramic alloy

Preparation of SiC-AlN Ceramic Alloy Powder by Direct Reaction Between Constituent Elements and Property Evaluation of Its Sintered Compacts.

Mechanical Properties of AlN-SiC Ceramic Composites Synthesized by Pressureless Sintering and Post-HIP Treatment.

High-Temperature Strength of Sic-Aln Solid-Solutions and Composites As Evaluated by Small Punch Tests

Pressureless Sintering and High-Temperature Strength of SiC-AlN Ceramics

Synthesis of SiC-AlN Ceramic Alloy Powder by the Direct Reactions Between the Constituent Elements.

Sintering And Mechanical Properties Of Aln-Rich Ceramics In The Sic-Aln System

Synthesis of SiC-AlN Powder and Characterization of Its HIP-Sintered Compacts.

Enhanced thermal shock resistance of BN-based composites sintered by hot-pressing with the introduction of nano oxides

High-temperature Deformation Behavior of SiC-AlN Ceramic Alloys with Fine-grained Microstructure.

Reaction Synthesis of SiC-AlN Ceramic Alloys

Phase evolution mechanism of SiC-Al-Si composite under flowing nitrogen at 1600 °C

Study on the mechanical properties and microstructure of Al2O3/nano-SiC multiphase ceramics

SiC and ZrN Nano-Particulate Reinforced AlON Composites: Preparation, Mechanical Properties and Toughening Mechanisms

Synthesis and properties of AIN-SiC-TiB2 ceramics by SHS-HIP

Preparation and characterization of medium entropy alloy CrCoNi toughened SiC ceramics

Nano-Phase and SiC–Si Spherical Microstructure in SiC/Al-50Si Composites Solidified under High Pressure

Formation mechanism of AlN-SiC solid solution with multiple morphologies in Al-Si-SiC composites under flowing nitrogen at 1300 °C

Carbothermally prepared nanophase SiC/ Si3N4 composite powders and densified parts

Significant improvements of the relative density, microhardness, and fracture toughness of SiC via the addition of Ni3Al and Mg2Si