Abstract:The non-oxide-reinforced phase AlN-SiC solid solution with high performance was successfully synthesized in the resin-bonded Al-Si-SiC composites under flowing nitrogen at 1300 °C. The AlN-SiC solid solution was synthesized by three paths of liquid-solid, gas-solid and gas-gas reactions through modulation of Al/Si ratio, and controllable microstructure of AlN-SiC solid solution was attained. The phase composition and microstructure of the sintered samples were characterized by XRD and SEM, combined with thermodynamics, the formation mechanism of AlN-SiC solid solution was investigated and the reaction model was established. Al was not detected while Si was detested by XRD. Granular, short columnar and whisker-like AlN-SiC solid solution were generated and their positions varied. As the temperature increases, the partial pressure of oxygen decreases due to the oxidation of Al, Si and SiC on the surface of the sample, inside the sample, the active oxidation takes place, generating Al2O(g), SiO(g) and CO(g). Due to the low oxygen partial pressure, Al is preferentially nitrided to form a thin AlN layer on its surface. The AlN layer is broken as the temperature increases, then liquid Al with carbon from resin begins to flow, leaving the residual shell of AlN in situ. When it flows to the surface of Si, Al-Sialloy is formed locally inside the Si particles under the wetting effect of C, then hexagonal AlN-SiC solid solution is formed inside the Si shell. Part of SiO(g) + CO(g) diffuses into the interior of the AlN residual shell and reacts by aggregation to form a granular AlN-SiC solid solution in the shell wall; others diffuses into the pores of the sample for vapor deposition, and finally forms stacked hexagonal flaky whiskers. The in-situ generated of AlN-SiC solid solution with multiple morphologies in the composite plays a joint toughening effect, which can significantly enhance the comprehensive performance of the composite. In this experiment, the synthesis of AlN-SiC solid solution without sintering aids under normal pressure at a low temperature. It is expected to be applied to the blast furnace and to realize the longevity of blast furnace.

Reaction Synthesis of SiC-AlN Ceramic Alloys

Synthesis of SiC-AlN Ceramic Alloy Powder by the Direct Reactions Between the Constituent Elements.

Preparation of SiC-AlN Ceramic Alloy Powder by Direct Reaction Between Constituent Elements and Property Evaluation of Its Sintered Compacts.

Synthesis of SiC-AlN Powder and Characterization of Its HIP-Sintered Compacts.

Preparation and mechanical properties of SiC-AlN ceramic alloy

Structural Formation and Mechanism in Combustion Synthesis of Nitrogen Ceramics (AIN, Si<sub>3</sub>N<sub>4</sub> and AIN-SiC)

In-Situ Reactive Synthesis of AlN-SiC Composites and Solid Solutions

Reaction Synthesis of Ceramic Composites Containing In Situ Formed Boron Nitride as Dispersed Phase

Mechanical Properties of SiC-AlN Single-Phase Alloys and Two-Phase Composites.

Synthesis of SiC-AIN ceramic alloy by reaction sintering and its HIP-densification

RESEARCH ON THE REACTION SYNTHESIS OF AlN-BASED CERAMICS WITH THE ADDITION OF Y2O3

In-situ synthesis of nano SiC particles in Al–Si–C system at 750 °C

In Situ Reactive Synthesis and Phase Stability Investigation in the AlN-SiC System

Reaction Synthesis of Ti3SiC2 from Mixture of Elemental Powders

Study on In-Situ Reaction Synthesis and Mechanical Properties of Si2N2O Ceramic

Synthesis and Consolidation of Composite Materials in the SiC–Si3N4–Si2N2O System

Formation mechanism of AlN-SiC solid solution with multiple morphologies in Al-Si-SiC composites under flowing nitrogen at 1300 °C

Combustion synthesis of AlN-SIC solid solutions

Synthesis mechanism of AlN–SiC solid solution reinforced Al2O3 composite by two-step nitriding of Al–Si3N4–Al2O3 compact at 1500 °C

Synthesis of Ti3SiC2 Powder by Mechanical Alloying and Mechanical Property of the Sintered Compacts.

Synthesis and properties of porous SiN/SiC nanocomposites by carbothermal reaction between SiN and carbon