Abstract:AlN is regarded as a promising ceramic material for high performance structural and high temperature applications due to its superior properties such as high thermal conductivity, excellent stability and wear resistance. However, challenges remain in fabricating AlN ceramics with high strength and high thermal shock resistance. In this work, AlN/YAlO3 composites with different YAlO3 contents (3–10 wt%) were prepared by a simple pressureless sintering method, and the impact of YAlO3 content on mechanical properties and thermal shock resistance of AlN/YAlO3 composites was investigated. Results show that the grain growth of AlN is inhibited and the densification is improved with the addition of 3 wt% and 5 wt% YAlO3. Hence, the flexural strength and fracture toughness of AlN/YAlO3 composites are improved due to the grain refinement and compactness enhancement, and the highest value, 369 MPa and 3.84 MPa m1/2, are reached by the AlN-5 wt% YAlO3 composite. Moreover, the thermal shock resistance was assessed through theoretical forecast and cyclic thermal shock tests over a temperature range between 1000 °C and 1600 °C. Comparing with pure AlN, the thermal stress damage resistance parameters (R IV ) of AlN/YAlO3 composites were increased, while their residual strengths and retention ratios after 10–50 cycles of thermal shock tests maintained a higher level as well. Microstructure analysis revealed that the thermal shock resistance of AlN/YAlO3 composites was evidently improved attributing to various strengthening mechanisms such as crack deflection, crack branching and microcrack toughening.

RESEARCH ON THE REACTION SYNTHESIS OF AlN-BASED CERAMICS WITH THE ADDITION OF Y2O3

Raction synthesis of Y2O3/A1N ceramic and mechanism of densification

Structural Formation and Mechanism in Combustion Synthesis of Nitrogen Ceramics (AIN, Si<sub>3</sub>N<sub>4</sub> and AIN-SiC)

Effects of YH2 addition on pressureless sintered AlN ceramics

COMBUSTION SYNTHFSIS AND DENSIFICATION BY GAS HOT ISOSTATIC PRESSURE OF AIN- TiB2 CERAMIC WITHOUT ENVELOPE

Effect of Additive Sm2O3 on Synthesizing AlN Ceramics at High Pressure

Effect of Y2o3-Al2o3 Additive on the Phase Formation and Densification Process of in Situ Sic-Bn Composite

Effects of Y2O3 and Yttrium Aluminates As Sintering Additives on the Thermal Conductivity of AlN Ceramic Substrates

Effect of Y2O3 on low temperature sintering and thermal conductivity of AlN ceramics

Microstructure and thermal conductivity of AlN ceramics with ultra-fine Y2O3 powder addition

Effect of Nitrogen Pressure and Additives on Combustion Synthesis of Rod-Like Yttrium α-SiAlON Crystals

Preparation of SiC-AlN Ceramic Alloy Powder by Direct Reaction Between Constituent Elements and Property Evaluation of Its Sintered Compacts.

Synthesis of SiC-AlN Ceramic Alloy Powder by the Direct Reactions Between the Constituent Elements.

Preparation of Si3N4 Ceramics with 3 wt % Y2O3–Al2O3 (2 : 1, 1 : 1, 3 : 5) Additions by Spark Plasma Sintering

Reaction Synthesis of Ceramic Composites Containing In Situ Formed Boron Nitride as Dispersed Phase

YAlO3 reinforced AlN composite ceramics with significantly improved mechanical properties and thermal shock resistance

Effect of AlN and ZrO2 on the Microstructure and Property of the 2Si-B-3c-n Ceramic

Densification and comprehensive properties of h-BN-based refractories with in-situ formation of Y3Al5O12

Reaction Synthesis of SiC-AlN Ceramic Alloys

Synthesis of nearly spherical AlN particles by an in-situ nitriding combustion route