Abstract:The non-oxide-reinforced phase AlN-SiC solid solution with high performance was successfully synthesized in the resin-bonded Al-Si-SiC composites under flowing nitrogen at 1300 °C. The AlN-SiC solid solution was synthesized by three paths of liquid-solid, gas-solid and gas-gas reactions through modulation of Al/Si ratio, and controllable microstructure of AlN-SiC solid solution was attained. The phase composition and microstructure of the sintered samples were characterized by XRD and SEM, combined with thermodynamics, the formation mechanism of AlN-SiC solid solution was investigated and the reaction model was established. Al was not detected while Si was detested by XRD. Granular, short columnar and whisker-like AlN-SiC solid solution were generated and their positions varied. As the temperature increases, the partial pressure of oxygen decreases due to the oxidation of Al, Si and SiC on the surface of the sample, inside the sample, the active oxidation takes place, generating Al2O(g), SiO(g) and CO(g). Due to the low oxygen partial pressure, Al is preferentially nitrided to form a thin AlN layer on its surface. The AlN layer is broken as the temperature increases, then liquid Al with carbon from resin begins to flow, leaving the residual shell of AlN in situ. When it flows to the surface of Si, Al-Sialloy is formed locally inside the Si particles under the wetting effect of C, then hexagonal AlN-SiC solid solution is formed inside the Si shell. Part of SiO(g) + CO(g) diffuses into the interior of the AlN residual shell and reacts by aggregation to form a granular AlN-SiC solid solution in the shell wall; others diffuses into the pores of the sample for vapor deposition, and finally forms stacked hexagonal flaky whiskers. The in-situ generated of AlN-SiC solid solution with multiple morphologies in the composite plays a joint toughening effect, which can significantly enhance the comprehensive performance of the composite. In this experiment, the synthesis of AlN-SiC solid solution without sintering aids under normal pressure at a low temperature. It is expected to be applied to the blast furnace and to realize the longevity of blast furnace.

Preparation and mechanical properties of SiC-AlN ceramic alloy

Mechanical Properties of SiC-AlN Single-Phase Alloys and Two-Phase Composites.

Preparation of SiC-AlN Ceramic Alloy Powder by Direct Reaction Between Constituent Elements and Property Evaluation of Its Sintered Compacts.

Synthesis of SiC-AlN Ceramic Alloy Powder by the Direct Reactions Between the Constituent Elements.

Optimization of Microstructure to Improve Si3n4 Ceramics with Thermal Conductivity and Mechanical Properties: Effect of Si and Α-Si3n4 Powder Composition

Synthesis of SiC-AlN Powder and Characterization of Its HIP-Sintered Compacts.

Pressureless Sintering and High-Temperature Strength of SiC-AlN Ceramics

Sintering And Mechanical Properties Of Aln-Rich Ceramics In The Sic-Aln System

Reaction Synthesis of SiC-AlN Ceramic Alloys

Significant improvements of the relative density, microhardness, and fracture toughness of SiC via the addition of Ni3Al and Mg2Si

Influence of α-Si3N4 coarse powder on densification, microstructure, mechanical properties, and thermal behavior of silicon nitride ceramics

Preparation, microstructure and ion-irradiation damage behavior of Al4SiC4-added SiC ceramics

High-temperature Deformation Behavior of SiC-AlN Ceramic Alloys with Fine-grained Microstructure.

Mechanical Properties of AlN-SiC Ceramic Composites Synthesized by Pressureless Sintering and Post-HIP Treatment.

Enhanced mechanical properties of R–SiC honeycomb ceramics with in situ AlN–SiC solid solution

Synthesis and Consolidation of Composite Materials in the SiC–Si3N4–Si2N2O System

Effects of SiC contents on the microstructure and mechanical properties of Al4SiC4–SiC ceramic composites

Effect Of Aln Content On The Pressureless Sintering Behaviors Of Sic-Aln Multiphase Ceramics

High-Temperature Strength of Sic-Aln Solid-Solutions and Composites As Evaluated by Small Punch Tests

Formation mechanism of AlN-SiC solid solution with multiple morphologies in Al-Si-SiC composites under flowing nitrogen at 1300 °C

Study on the mechanical properties and microstructure of Al2O3/nano-SiC multiphase ceramics