Abstract:Alpha phase silicon nitride (α-Si3N4) powders were synthesized by combustion reaction of the in-situ nano-SiO2 coated Si and Si3N4 reactants with pressurized nitrogen. The combustion temperature profile as well as the product phase composition and morphology were investigated. Regardless of the combustion temperature reached as high as 1800 °C, up to 86 wt% α-Si3N4 was obtained in the combustion-synthesized product from the reactants with only 6 wt% SiO2 addition, which is three times higher than that of without SiO2 coating, meanwhile, the morphology of Si3N4 grains changed from rod-like to equiaxed grain,indicating the in-situ coated SiO2 tailored the nitridation reaction path of Si successfully by enhancing the silicon monoxide (SiO) gas phase formation.
What problem does this paper attempt to address?
The problem that this paper attempts to solve is how to increase the content of α - Si₃N₄ (alpha - silicon nitride) and optimize its microstructure when preparing α - Si₃N₄ powder by combustion synthesis in a high - temperature nitrogen environment. In traditional methods, due to the extremely high combustion temperature (which can reach above 1800 °C), the product is easily converted into β - Si₃N₄, and the performance of β - Si₃N₄ is not as good as that of α - Si₃N₄. In addition, in order to promote the formation of α - Si₃N₄, corrosive ammonium salts are usually required to be added, which not only harms the environment but also may damage the equipment. Therefore, this research aims to find a non - corrosive green additive to effectively increase the yield and purity of α - Si₃N₄.
Specifically, the author has successfully increased the content of α - Si₃N₄ and changed the microstructure of the product by introducing a nano - SiO₂ coating. The experimental results show that even without reducing the combustion temperature, by adding a small amount of SiO₂ (6 wt%), the content of α - Si₃N₄ can be increased to 86%, which is much higher than the situation without adding SiO₂ (24%). At the same time, the morphology of Si₃N₄ particles has changed from acicular to equiaxed grains, which indicates that the SiO₂ coating effectively promotes the generation of SiO gas, thereby enhancing the gas - phase reaction path, reducing the formation of liquid - phase Si, and avoiding the growth of β - Si₃N₄.
In conclusion, this research provides a new and environmentally - friendly method for preparing high - purity α - Si₃N₄ powder and has important application prospects.