Abstract:AlN-SiC solid solutions were successfully prepared by combustion synthesis from a mixture of Al, Si and C under high-pressure nitrogen. The reaction mechanism for combustion synthesis of AlN-SiC solid solutions is as follows: Al and Si melt at the front of combustion wave; carbon black is mixed into the molten mixture; Al reacts with nitrogen to form AlN; both liquid Si and silicon vapor (from evaporation of Si powder due to the high exothermic heat of the reactions, or from the decomposition of intermediate Si3N4) react with C to form SiC. Simultaneously, Si and C (or SiC) diffuse into the AlN crystal lattice directly to form an AlN-rich solid solution, and Al (or AlN) diffuses into the SiC crystal lattice directly to form a SiC-rich solid solution. The strengthening of the atomic bonding within the basal planes of the AlN-SiC solid solution, and a weakening of the bonds between the basal planes due to interdiffusion of AlN and SiC hinders the nucleation on the 0001 planes and promotes the growth of the 0001 planes, with the result that AlN-SiC solid solution tends to grow in the form of platelets. The combustion synthesised AlN-SiC solid solution spinodally decomposes into AlN-rich and SiC-rich domains during cooling. Both the AlN-rich and the SiC-rich domains share the same <0002> zone axis and their reciprocal planes perpendicular to the <0002> zone axis are rotated 30° clockwise around it.

Combustion Synthesis of Si<sub>3</sub>N<sub>4</sub> from Si/NH<sub>4</sub>Cl at Low Nitrogen Pressure

Combustion Synthesis of Si<sub>3</sub>N<sub>4</sub> from Si/NH<sub>4</sub>Cl at Low Nitrogen Pressure

Combustion Synthesis of Α-Si3n4 with the Addition of NH4Cl

Structural Formation and Mechanism in Combustion Synthesis of Nitrogen Ceramics (AIN, Si<sub>3</sub>N<sub>4</sub> and AIN-SiC)

Combustion synthesis of α-Si3N4 powders using in-situ nano-SiO2 coated Si and Si3N4 reactants

Preheating-assisted Combustion Synthesis of Β-Si3n4 Powders at Low N2 Pressure

Combustion Synthesis of AlN–SiC Solid Solution Particles

Combustion Synthesis of SiC Nanosized Powders at Low Nitrogen Pressure

On the Progress of Combustion Synthesis of Si<sub>3</sub>N<sub>4</sub> Ceramic: From Laboratory Research to Industrial Production

Combustion Synthesis of MgSiN2 Powders and Si3N4‐MgSiN2 Composite Powders: Effects of Processing Parameters

Synthesis of Si3N4–TiN–SiC Composites by Combustion Reaction under High Nitrogen Pressures

On the Progress of Combustion Synthesis of Si3n4 Ceramic: from Laboratory Research to Industrial Production

Combustion synthesis Si3N4 powders by using activation process

Combustion synthesis of well-dispersed rod-like -Si<sub>3</sub>N<sub>4</sub> crystals by the addition of carbon

Combustion Synthesis of Nanosized Β-Sic Powder on a Large Scale

Combustion synthesis of AlN-SIC solid solutions

Coarse‐grained Β‐si3n4 Powders Prepared by Combustion Synthesis

Effect of the Diluent on Combustion Synthesis of Silicon Nitride

Coarse‐grained β‐Si 3 N 4 powders prepared by combustion synthesis

Microstructure and Thermo‐Kinetics Analysis in Combustion Synthesis of Si3N4 with High α‐Phase Content

Combustion Synthesis of Α-Si3n4 with Green Additives

Combustion Synthesis of Si<sub>3</sub>N<sub>4</sub> from Si/NH<sub>4</sub>Cl at Low Nitrogen Pressure

Combustion Synthesis of Si&lt;sub&gt;3&lt;/sub&gt;N&lt;sub&gt;4&lt;/sub&gt; from Si/NH&lt;sub&gt;4&lt;/sub&gt;Cl at Low Nitrogen Pressure

Combustion Synthesis of Α-Si3n4 with the Addition of NH4Cl

Structural Formation and Mechanism in Combustion Synthesis of Nitrogen Ceramics (AIN, Si<sub>3</sub>N<sub>4</sub> and AIN-SiC)

Combustion synthesis of α-Si3N4 powders using in-situ nano-SiO2 coated Si and Si3N4 reactants

Preheating-assisted Combustion Synthesis of Β-Si3n4 Powders at Low N2 Pressure

Combustion Synthesis of AlN–SiC Solid Solution Particles

Combustion Synthesis of SiC Nanosized Powders at Low Nitrogen Pressure

On the Progress of Combustion Synthesis of Si&lt;sub&gt;3&lt;/sub&gt;N&lt;sub&gt;4&lt;/sub&gt; Ceramic: From Laboratory Research to Industrial Production

Combustion Synthesis of MgSiN2 Powders and Si3N4‐MgSiN2 Composite Powders: Effects of Processing Parameters

Synthesis of Si3N4–TiN–SiC Composites by Combustion Reaction under High Nitrogen Pressures

On the Progress of Combustion Synthesis of Si3n4 Ceramic: from Laboratory Research to Industrial Production

Combustion synthesis Si3N4 powders by using activation process

Combustion synthesis of well-dispersed rod-like -Si<sub>3</sub>N<sub>4</sub> crystals by the addition of carbon

Combustion Synthesis of Nanosized Β-Sic Powder on a Large Scale

Combustion synthesis of AlN-SIC solid solutions

Coarse‐grained Β‐si3n4 Powders Prepared by Combustion Synthesis

Effect of the Diluent on Combustion Synthesis of Silicon Nitride

Coarse‐grained β‐Si 3 N 4 powders prepared by combustion synthesis

Microstructure and Thermo‐Kinetics Analysis in Combustion Synthesis of Si3N4 with High α‐Phase Content

Combustion Synthesis of Α-Si3n4 with Green Additives

Combustion Synthesis of Si<sub>3</sub>N<sub>4</sub> from Si/NH<sub>4</sub>Cl at Low Nitrogen Pressure

On the Progress of Combustion Synthesis of Si<sub>3</sub>N<sub>4</sub> Ceramic: From Laboratory Research to Industrial Production