Abstract:Herein, Si3N4 powders of comparatively high α‐phase but with distinct morphologies, especially α‐Si3N4 fibers, were successfully prepared by a developed combustion synthesis (CS) strategy. Different proportions of Fe and Fe2O3 were innovatively doped in reactants as additives to control the phase constitution and their relative percentage, as well as morphologies of final microstructures. One step further, the effects of Fe‐contained impurities on the CS process were rationally proposed and verified based on a series of meticulous designed experiments. It turns out that two contradictory effects of metal Fe on the formation of α‐Si3N4 synergistically play vital roles in the CS reaction. The existence of metal Fe can accelerate the crystallization of the amorphous SiO2, which act as protection layer outside the Si powders and subsequently promote the generation of gaseous SiO. These gaseous SiO easily reacts with N2 and eventually form α‐Si3N4. On the other hand, the formation of β‐Si3N4 will be promoted by the assistance of some liquid phases, and in this case, they mainly come from the reaction between Fe and Si. For this study, when the content of doped Fe is below 2 mol%, the prior effect on promoting α‐phase content is pronounced. Otherwise, the latter dominates the CS process as the content of Fe additive is further increased above 2 mol%. In a different way, Fe2O3 mainly encourages the formation of β phase through the large amount of newly generated liquid phases, although the reduced SiO2 and Fe may still promote the α/β ratio on some extent.

Microstructure and Thermo‐Kinetics Analysis in Combustion Synthesis of Si3N4 with High α‐Phase Content

Structural Formation and Mechanism in Combustion Synthesis of Nitrogen Ceramics (AIN, Si<sub>3</sub>N<sub>4</sub> and AIN-SiC)

Optimization of Microstructure to Improve Si3n4 Ceramics with Thermal Conductivity and Mechanical Properties: Effect of Si and Α-Si3n4 Powder Composition

Combustion synthesis of α-Si3N4 powders using in-situ nano-SiO2 coated Si and Si3N4 reactants

Crystal Growth In The Combustion Synthesis Of -Si3n4 Using Si With Different Particle Sizes

Effect of Fe‐Contained Species on the Preparation of Α‐si3n4 Fibers in Combustion Synthesis

MICROSTRUCTURE OF Si3N4-TiN-SiC CERAMICS DURING COMBUSTION SYNTHESIS PROCESS

Synthesis of Si 3 N 4 powder with tunable α/β-Si 3 N 4 content from waste silica fume using carbothermal reduction nitridation

Phase transformation and growth of rod-like α-SiAlON particles during combustion synthesis

Effects of starting compositions on the phase composition and microstructure of Yb α-SiAlON prepared by combustion synthesis

Combustion synthesis Si3N4 powders by using activation process

Coarse‐grained β‐Si 3 N 4 powders prepared by combustion synthesis

Combustion Synthesis of Α-Si3n4 with the Addition of NH4Cl

On the Progress of Combustion Synthesis of Si<sub>3</sub>N<sub>4</sub> Ceramic: From Laboratory Research to Industrial Production

Effect of Impurities MgO, CaO, Al2O3, AlN and Al on Α/β Ratio in Combustion Synthesis of Α-Si3n4

Synthesis of Spherical Si3N4 Powders by Liquid‐phase Modified Carbothermal Reduction and Nitridation

Combustion Synthesis of MgSiN2 Powders and Si3N4‐MgSiN2 Composite Powders: Effects of Processing Parameters

Study on the Combustion Synthesis of Si3N4-SiC-TiN Ceramics

Synthesis of Si<sub>3</sub>N<sub>4</sub>-TiN-SiC Composites by Combustion Reaction under High Nitrogen Pressures

Reaction mechanisms of combustion synthesis of Si3N4 -SiC -TiN ceramics

On the Progress of Combustion Synthesis of Si3n4 Ceramic: from Laboratory Research to Industrial Production