Abstract:Herein, Si3N4 powders of comparatively high α‐phase but with distinct morphologies, especially α‐Si3N4 fibers, were successfully prepared by a developed combustion synthesis (CS) strategy. Different proportions of Fe and Fe2O3 were innovatively doped in reactants as additives to control the phase constitution and their relative percentage, as well as morphologies of final microstructures. One step further, the effects of Fe‐contained impurities on the CS process were rationally proposed and verified based on a series of meticulous designed experiments. It turns out that two contradictory effects of metal Fe on the formation of α‐Si3N4 synergistically play vital roles in the CS reaction. The existence of metal Fe can accelerate the crystallization of the amorphous SiO2, which act as protection layer outside the Si powders and subsequently promote the generation of gaseous SiO. These gaseous SiO easily reacts with N2 and eventually form α‐Si3N4. On the other hand, the formation of β‐Si3N4 will be promoted by the assistance of some liquid phases, and in this case, they mainly come from the reaction between Fe and Si. For this study, when the content of doped Fe is below 2 mol%, the prior effect on promoting α‐phase content is pronounced. Otherwise, the latter dominates the CS process as the content of Fe additive is further increased above 2 mol%. In a different way, Fe2O3 mainly encourages the formation of β phase through the large amount of newly generated liquid phases, although the reduced SiO2 and Fe may still promote the α/β ratio on some extent.

Combustion Synthesis of Α-Si3n4 with Green Additives

Combustion Synthesis of Α-Si3n4 with the Addition of NH4Cl

Structural Formation and Mechanism in Combustion Synthesis of Nitrogen Ceramics (AIN, Si<sub>3</sub>N<sub>4</sub> and AIN-SiC)

Combustion synthesis of α-Si3N4 powders using in-situ nano-SiO2 coated Si and Si3N4 reactants

On the Progress of Combustion Synthesis of Si<sub>3</sub>N<sub>4</sub> Ceramic: From Laboratory Research to Industrial Production

Combustion synthesis Si3N4 powders by using activation process

On the Progress of Combustion Synthesis of Si3n4 Ceramic: from Laboratory Research to Industrial Production

Combustion synthesis of well-dispersed rod-like -Si<sub>3</sub>N<sub>4</sub> crystals by the addition of carbon

In Situ Combustion Synthesis of Composite Ceramics

Combustion synthesis of fine aluminum nitride powders under micropositive N 2 pressure with water additive

Combustion Synthesis of MgSiN2 Powders and Si3N4‐MgSiN2 Composite Powders: Effects of Processing Parameters

Combustion Synthesis Of Beta-Si3n4 And Beta-Sialon With Elongated Prismatic Micro-Crystals By Adding Srco3 And Nh4f

Effects of diazenedicarboxamide additive on the content of α-Si3N4 synthesized by combustion method

Combustion Synthesis of Si<sub>3</sub>N<sub>4</sub> from Si/NH<sub>4</sub>Cl at Low Nitrogen Pressure

Combustion Synthesis of AlN–SiC Solid Solution Particles

Effect of Impurities MgO, CaO, Al2O3, AlN and Al on Α/β Ratio in Combustion Synthesis of Α-Si3n4

Combustion Synthesis of β-Si<sub>3</sub>N<sub>4</sub> and β-SiAlON with Elongated Prismatic Micro-Crystals by Adding SrCO<sub>3</sub> and NH<sub>4</sub>F

Effect of Fe‐Contained Species on the Preparation of Α‐si3n4 Fibers in Combustion Synthesis

Combustion Synthesis of Si<sub>3</sub>N<sub>4</sub> from Si/NH<sub>4</sub>Cl at Low Nitrogen Pressure

Combustion synthesis of AlN-SIC solid solutions

Effect of Diluents and NH4F Additive on the Combustion Synthesis of Yb Α-Sialon

Combustion Synthesis of Α-Si3n4 with Green Additives

Combustion Synthesis of Α-Si3n4 with the Addition of NH4Cl

Structural Formation and Mechanism in Combustion Synthesis of Nitrogen Ceramics (AIN, Si<sub>3</sub>N<sub>4</sub> and AIN-SiC)

Combustion synthesis of α-Si3N4 powders using in-situ nano-SiO2 coated Si and Si3N4 reactants

On the Progress of Combustion Synthesis of Si&lt;sub&gt;3&lt;/sub&gt;N&lt;sub&gt;4&lt;/sub&gt; Ceramic: From Laboratory Research to Industrial Production

Combustion synthesis Si3N4 powders by using activation process

On the Progress of Combustion Synthesis of Si3n4 Ceramic: from Laboratory Research to Industrial Production

Combustion synthesis of well-dispersed rod-like -Si<sub>3</sub>N<sub>4</sub> crystals by the addition of carbon

In Situ Combustion Synthesis of Composite Ceramics

Combustion synthesis of fine aluminum nitride powders under micropositive N 2 pressure with water additive

Combustion Synthesis of MgSiN2 Powders and Si3N4‐MgSiN2 Composite Powders: Effects of Processing Parameters

Combustion Synthesis Of Beta-Si3n4 And Beta-Sialon With Elongated Prismatic Micro-Crystals By Adding Srco3 And Nh4f

Effects of diazenedicarboxamide additive on the content of α-Si3N4 synthesized by combustion method

Combustion Synthesis of Si&lt;sub&gt;3&lt;/sub&gt;N&lt;sub&gt;4&lt;/sub&gt; from Si/NH&lt;sub&gt;4&lt;/sub&gt;Cl at Low Nitrogen Pressure

Combustion Synthesis of AlN–SiC Solid Solution Particles

Effect of Impurities MgO, CaO, Al2O3, AlN and Al on Α/β Ratio in Combustion Synthesis of Α-Si3n4

Combustion Synthesis of β-Si<sub>3</sub>N<sub>4</sub> and β-SiAlON with Elongated Prismatic Micro-Crystals by Adding SrCO<sub>3</sub> and NH<sub>4</sub>F

Effect of Fe‐Contained Species on the Preparation of Α‐si3n4 Fibers in Combustion Synthesis

Combustion Synthesis of Si<sub>3</sub>N<sub>4</sub> from Si/NH<sub>4</sub>Cl at Low Nitrogen Pressure

Combustion synthesis of AlN-SIC solid solutions

Effect of Diluents and NH4F Additive on the Combustion Synthesis of Yb Α-Sialon

On the Progress of Combustion Synthesis of Si<sub>3</sub>N<sub>4</sub> Ceramic: From Laboratory Research to Industrial Production

Combustion Synthesis of Si<sub>3</sub>N<sub>4</sub> from Si/NH<sub>4</sub>Cl at Low Nitrogen Pressure