Abstract:AlN-SiC solid solution particles with a variety of morphologies including faceted polyhedrons with or without ledges; hexagonal platelets; hexagonal columns with a hexagonal plate or a pyramidal cap; and interpenetrating cones, have been found in the combustion products of a mixture of Al, Si, and carbon black under a nitrogen pressure of 10 MPa. Combustion temperature (the growth temperature of crystals) is the most important factor controlling the morphology of crystals formed in the combustion product. When temperatures are close to the melting point of the solid solutions, a small driving force for nucleation and long distances of surface migration make nucleation on the basal plane difficult, and thus the solid solution particles tend to grow as platelets. Supersaturation is the second key factor influencing crystal growth. At relatively low temperatures, a low supersaturation at the large pores renders nucleation difficult and the solid solution particles tend to grow as platelets. At relatively low temperatures and high supersaturation, a relatively high driving force for nucleation and short mean distances of surface migration promote the growth of AlN-SiC solid solutions as polyhedrons. The formation of the ledges on the polyhedral particles is attributed to the differences in the evaporation rates and the deposition rates between Al and Si. At relatively low temperatures and an intermediate supersaturation, the solid solution particles grow as prismatic columns. The formation of the prismatic columns with a hexagonal plate, or a pyramidal cap, is attributed to a sudden change of temperature during combustion. A possible growth mechanism for the AlN-SiC solid solution cones is proposed.

Combustion Synthesis Of Beta-Si3n4 And Beta-Sialon With Elongated Prismatic Micro-Crystals By Adding Srco3 And Nh4f

Combustion Synthesis of β-Si<sub>3</sub>N<sub>4</sub> and β-SiAlON with Elongated Prismatic Micro-Crystals by Adding SrCO<sub>3</sub> and NH<sub>4</sub>F

Structural Formation and Mechanism in Combustion Synthesis of Nitrogen Ceramics (AIN, Si<sub>3</sub>N<sub>4</sub> and AIN-SiC)

Combustion synthesis of well-dispersed rod-like -Si<sub>3</sub>N<sub>4</sub> crystals by the addition of carbon

Coarse‐grained Β‐si3n4 Powders Prepared by Combustion Synthesis

Coarse‐grained β‐Si 3 N 4 powders prepared by combustion synthesis

Combustion synthesis of α-Si3N4 powders using in-situ nano-SiO2 coated Si and Si3N4 reactants

Effect of Diluents and NH4F Additive on the Combustion Synthesis of Yb Α-Sialon

Gel-cast-foam-assisted Combustion Synthesis of Elongated Β-Si3n4 Crystals and Their Effects on Improving the Thermal Conductivity of Silicone Composites

Effects of starting compositions on the phase composition and microstructure of Yb α-SiAlON prepared by combustion synthesis

Combustion Synthesis of Α-Si3n4 with the Addition of NH4Cl

Effect of Nitrogen Pressure and Additives on Combustion Synthesis of Rod-Like Yttrium α-SiAlON Crystals

Combustion synthesis Si3N4 powders by using activation process

Preparation of Ca α-SiAlON powders with rod-like crystals by combustion synthesis

Preparation of (ca+m) (m=mg, Yb, Sr) Co-Doped Α-Sialon Powders by Combustion Synthesis

Combustion synthesis of AlN-SIC solid solutions

Growth Mechanisms for SiC-AlN Solid Solution Crystals Prepared by Combustion Synthesis

Fabrication of yttrium-stabilized α -SiAlON powders with rod-like crystals by combustion synthesis

Phase transformation and growth of rod-like α-SiAlON particles during combustion synthesis

Combustion Synthesis of Nanosized Β-Sic Powder on a Large Scale

Solid-state NMR and XRD study of α-SiAlON powders prepared by combustion synthesis