Abstract:Si3N4 ceramic with ultrafine fibrous grains are expected to exhibit remarkable mechanical properties. In this work, highly porous Si3N4 ceramic monoliths composed of ultrafine fibrous grains were developed via a novel vapor-solid carbothermal reduction nitridation (V-S CRN) reaction between SiO vapor and green bodies comprised of carbon nanotubes (CNTs), α-Si3N4 diluents and Y2O3 in a N2 atmosphere. The unique fibrous grains-interconnected structure was developed through in-situ formation of Si3N4 and following liquid phase sintering. The porous Si3N4 monoliths with porosity of 61–78% was developed by controlling the contents of α-Si3N4 diluents and densities of the CNT green bodies. With increasing of the α-Si3N4 contents, Si3N4 fibrous grains with an aspect ratio of approximate or higher than 20 could be achieved, and the grains were gradually refined. For the samples with 40 wt% α-Si3N4, the minimum mean grain diameter and pore size of 164 nm and 0.79 μm were achieved, respectively, and the resultant porous Si3N4 monolith exhibited a flexural strength of as high as 73–102 MPa with the porosity of 61–73%, which is much higher than that of the reported in literature. The improvement of mechanical strength could be attributed to the densely interconnected bird's nests structure formed by the ultrafine fibrous grains. The effects of the α-Si3N4 diluents on the resulting porous Si3N4 monolith via this method were analyzed.

Gel-cast-foam-assisted Combustion Synthesis of Elongated Β-Si3n4 Crystals and Their Effects on Improving the Thermal Conductivity of Silicone Composites

Effects of Nitrogen Pressure and Diluent Content on the Morphology of Gel-Cast-foam-assisted Combustion Synthesis of Elongated Β-Si3n4 Particles

Optimization of Microstructure to Improve Si3n4 Ceramics with Thermal Conductivity and Mechanical Properties: Effect of Si and Α-Si3n4 Powder Composition

Combustion Synthesis Of Beta-Si3n4 And Beta-Sialon With Elongated Prismatic Micro-Crystals By Adding Srco3 And Nh4f

Combustion Synthesis of β-Si<sub>3</sub>N<sub>4</sub> and β-SiAlON with Elongated Prismatic Micro-Crystals by Adding SrCO<sub>3</sub> and NH<sub>4</sub>F

Gel casting and properties of porous silicon carbide/silicon nitride composite ceramics

Enhanced Thermal Conductivities of Epoxy Nanocomposites Via Incorporating In-Situ Fabricated Hetero-Structured SiC-BNNS Fillers

Preparation of <i>In Situ</i> Synthesized SiC Particles Reinforced Highly Porous Si<sub>3</sub>N<sub>4</sub> Ceramics by Gel-Casting

Combustion synthesis of well-dispersed rod-like -Si<sub>3</sub>N<sub>4</sub> crystals by the addition of carbon

Microstructure and properties of porous Si3N4 ceramics by gelcasting-self-propagating high-temperature synthesis (SHS)

Gelcasting Preparation of Porous Silicon Nitride Ceramics by Adjusting the Content of Monomers

Synthesis and Mechanical Properties of Highly Porous Ultrafine-Grain Si3N4 Ceramics Via Carbothermal Reduction-Nitridation Combined with Liquid Phase Sintering

Effect of In-Situ Formed MoSi2 on Phase Transformation and Thermal Diffusivity of Spark Plasma Sintered Silicon Nitride

SiC–Si3N4 composite with multi-laminate nanowires originated from oriented porous structure by freeze-casting

Preparation of in-situ synthesized SiC particles reinforced highly porous Si3N4 ceramics by gel-casting

Simultaneous improvement in porosity and strength of porous β-Si3N4 ceramics by formation of ultrafine fibrous grains

Fabrication of Si3N4 Ceramics with High Thermal Conductivity and Flexural Strength Via Novel Two-Step Gas-Pressure Sintering

Enhanced Thermal Conductivity of Silicon Carbide Nanowires (sicw)/epoxy Resin Composite with Segregated Structure

Preparation and Properties of Porous Silicon Carbide Ceramics Through Coat-Mix and Composite Additives Process

In‐situ combustion synthesis of spherical Si@Si3N4 granules

Preparation of the Novel B4C–SiC Composite Aerogel with High Compressive Strength and Low Thermal Conductivity