Abstract:AlN-SiC solid solution particles with a variety of morphologies including faceted polyhedrons with or without ledges; hexagonal platelets; hexagonal columns with a hexagonal plate or a pyramidal cap; and interpenetrating cones, have been found in the combustion products of a mixture of Al, Si, and carbon black under a nitrogen pressure of 10 MPa. Combustion temperature (the growth temperature of crystals) is the most important factor controlling the morphology of crystals formed in the combustion product. When temperatures are close to the melting point of the solid solutions, a small driving force for nucleation and long distances of surface migration make nucleation on the basal plane difficult, and thus the solid solution particles tend to grow as platelets. Supersaturation is the second key factor influencing crystal growth. At relatively low temperatures, a low supersaturation at the large pores renders nucleation difficult and the solid solution particles tend to grow as platelets. At relatively low temperatures and high supersaturation, a relatively high driving force for nucleation and short mean distances of surface migration promote the growth of AlN-SiC solid solutions as polyhedrons. The formation of the ledges on the polyhedral particles is attributed to the differences in the evaporation rates and the deposition rates between Al and Si. At relatively low temperatures and an intermediate supersaturation, the solid solution particles grow as prismatic columns. The formation of the prismatic columns with a hexagonal plate, or a pyramidal cap, is attributed to a sudden change of temperature during combustion. A possible growth mechanism for the AlN-SiC solid solution cones is proposed.

Combustion synthesis of well-dispersed rod-like -Si<sub>3</sub>N<sub>4</sub> crystals by the addition of carbon

Combustion Synthesis Of Beta-Si3n4 And Beta-Sialon With Elongated Prismatic Micro-Crystals By Adding Srco3 And Nh4f

Combustion Synthesis of β-Si<sub>3</sub>N<sub>4</sub> and β-SiAlON with Elongated Prismatic Micro-Crystals by Adding SrCO<sub>3</sub> and NH<sub>4</sub>F

Structural Formation and Mechanism in Combustion Synthesis of Nitrogen Ceramics (AIN, Si<sub>3</sub>N<sub>4</sub> and AIN-SiC)

Coarse‐grained Β‐si3n4 Powders Prepared by Combustion Synthesis

Coarse‐grained β‐Si 3 N 4 powders prepared by combustion synthesis

Preparation of SiC/Si3N4 composites with rod-like microstructure by combustion synthesis

Combustion Synthesis of Nanosized Β-Sic Powder on a Large Scale

Combustion synthesis of α-Si3N4 powders using in-situ nano-SiO2 coated Si and Si3N4 reactants

Controlled growth of SiC crystals in combustion synthesis

Combustion Synthesis of Α-Si3n4 with Green Additives

Combustion synthesis of AlN-SIC solid solutions

Combustion Synthesis of Si<sub>3</sub>N<sub>4</sub> from Si/NH<sub>4</sub>Cl at Low Nitrogen Pressure

Growth Mechanisms for SiC-AlN Solid Solution Crystals Prepared by Combustion Synthesis

Combustion Synthesis of Α-Si3n4 with the Addition of NH4Cl

Combustion Synthesis of Si<sub>3</sub>N<sub>4</sub> from Si/NH<sub>4</sub>Cl at Low Nitrogen Pressure

Combustion synthesis Si3N4 powders by using activation process

Crystal Growth In The Combustion Synthesis Of -Si3n4 Using Si With Different Particle Sizes

Combustion Synthesis of AlN–SiC Solid Solution Particles

Effect of Nitrogen Pressure and Additives on Combustion Synthesis of Rod-Like Yttrium α-SiAlON Crystals

Synthesis of Well-Dispersed Columnar Si 3 N 4 Using Carbothermal Reduction–nitridation Method

Combustion synthesis of well-dispersed rod-like -Si<sub>3</sub>N<sub>4</sub> crystals by the addition of carbon

Combustion Synthesis Of Beta-Si3n4 And Beta-Sialon With Elongated Prismatic Micro-Crystals By Adding Srco3 And Nh4f

Combustion Synthesis of β-Si<sub>3</sub>N<sub>4</sub> and β-SiAlON with Elongated Prismatic Micro-Crystals by Adding SrCO<sub>3</sub> and NH<sub>4</sub>F

Structural Formation and Mechanism in Combustion Synthesis of Nitrogen Ceramics (AIN, Si<sub>3</sub>N<sub>4</sub> and AIN-SiC)

Coarse‐grained Β‐si3n4 Powders Prepared by Combustion Synthesis

Coarse‐grained β‐Si 3 N 4 powders prepared by combustion synthesis

Preparation of SiC/Si3N4 composites with rod-like microstructure by combustion synthesis

Combustion Synthesis of Nanosized Β-Sic Powder on a Large Scale

Combustion synthesis of α-Si3N4 powders using in-situ nano-SiO2 coated Si and Si3N4 reactants

Controlled growth of SiC crystals in combustion synthesis

Combustion Synthesis of Α-Si3n4 with Green Additives

Combustion synthesis of AlN-SIC solid solutions

Combustion Synthesis of Si<sub>3</sub>N<sub>4</sub> from Si/NH<sub>4</sub>Cl at Low Nitrogen Pressure

Growth Mechanisms for SiC-AlN Solid Solution Crystals Prepared by Combustion Synthesis

Combustion Synthesis of Α-Si3n4 with the Addition of NH4Cl

Combustion Synthesis of Si&lt;sub&gt;3&lt;/sub&gt;N&lt;sub&gt;4&lt;/sub&gt; from Si/NH&lt;sub&gt;4&lt;/sub&gt;Cl at Low Nitrogen Pressure

Combustion synthesis Si3N4 powders by using activation process

Crystal Growth In The Combustion Synthesis Of -Si3n4 Using Si With Different Particle Sizes

Combustion Synthesis of AlN–SiC Solid Solution Particles

Effect of Nitrogen Pressure and Additives on Combustion Synthesis of Rod-Like Yttrium α-SiAlON Crystals

Synthesis of Well-Dispersed Columnar Si 3 N 4 Using Carbothermal Reduction–nitridation Method

Combustion Synthesis of Si<sub>3</sub>N<sub>4</sub> from Si/NH<sub>4</sub>Cl at Low Nitrogen Pressure