Abstract:An alternative method to incorporate nanometer-sized silicon carbide (SiC) particles into silicon nitride (Si3N4) powder was proposed and investigated experimentally. Novolac-type phenolic resin was dissolved in ethanol and mixed with Si3N4 powder. After drying and curing, the resin was converted to reactive carbon via pyrolysis, Si3N4 powder was partially reduced carbothermally using the pyrolyzed carbon, and nanometer-sized SIC particles were produced in situ at 1530 degrees-1610 degrees C in atmospheric nitrogen. At temperatures <1550 degrees C, the reduction rate was low and the SIC particles were very small; no SiC whiskers or barlike SIC was observed. At 1600 degrees C, the reduction rate was high and the reaction was close to completion after only 10 min, with the appearance of SiC whiskers as well as curved, barlike, and equiaxial SiC, all of which were dozens of nanometers in diameter; this size is greater than that at observed temperatures <1550 degrees C. A longer soaking time at 1600 degrees C led to agglomerates. SiC particles were close to the surface of the Si3N4 particles. The SiC content could be adjusted by changing the carbon content before reduction and the reduction temperature. A reaction mechanism that involved the decomposition of Si3N4 has been proposed.

Combustion Synthesis of SiC Nanosized Powders at Low Nitrogen Pressure

Combustion Synthesis of Nanosized Β-Sic Powder on a Large Scale

Preheating-assisted Combustion Synthesis of Β-Si3n4 Powders at Low N2 Pressure

High-pressure Synthesis of High-Performance Submicron-Sized Polycrystalline Β-Si3n4 Bulk Without Additives

Structural Formation and Mechanism in Combustion Synthesis of Nitrogen Ceramics (AIN, Si<sub>3</sub>N<sub>4</sub> and AIN-SiC)

Combustion Synthesis of Si<sub>3</sub>N<sub>4</sub> from Si/NH<sub>4</sub>Cl at Low Nitrogen Pressure

Combustion synthesis of α-Si3N4 powders using in-situ nano-SiO2 coated Si and Si3N4 reactants

Combustion Synthesis of Si<sub>3</sub>N<sub>4</sub> from Si/NH<sub>4</sub>Cl at Low Nitrogen Pressure

Coarse‐grained Β‐si3n4 Powders Prepared by Combustion Synthesis

On the Progress of Combustion Synthesis of Si<sub>3</sub>N<sub>4</sub> Ceramic: From Laboratory Research to Industrial Production

On the Progress of Combustion Synthesis of Si3n4 Ceramic: from Laboratory Research to Industrial Production

Combustion Synthesis of AlN–SiC Solid Solution Particles

Synthesis of Si3N4–TiN–SiC Composites by Combustion Reaction under High Nitrogen Pressures

Coarse‐grained β‐Si 3 N 4 powders prepared by combustion synthesis

Studies of synthesizing the SiC nanometer powders by chemical vapor reaction

Synthesis of Silicon Nitride/Silicon Carbide Nanocomposite Powders through Partial Reduction of Silicon Nitride by Pyrolyzed Carbon

Combustion synthesis Si3N4 powders by using activation process

Combustion synthesis of well-dispersed rod-like -Si<sub>3</sub>N<sub>4</sub> crystals by the addition of carbon

Effect of Nitrogen Pressure and Additives on Combustion Synthesis of Rod-Like Yttrium α-SiAlON Crystals

Effects of Pelletization of Reactants and Diluents on the Combustion Synthesis of Si3N4 Powder

Synthesis of nanocrystalline silicon carbide powders

Combustion Synthesis of SiC Nanosized Powders at Low Nitrogen Pressure

Combustion Synthesis of Nanosized Β-Sic Powder on a Large Scale

Preheating-assisted Combustion Synthesis of Β-Si3n4 Powders at Low N2 Pressure

High-pressure Synthesis of High-Performance Submicron-Sized Polycrystalline Β-Si3n4 Bulk Without Additives

Structural Formation and Mechanism in Combustion Synthesis of Nitrogen Ceramics (AIN, Si<sub>3</sub>N<sub>4</sub> and AIN-SiC)

Combustion Synthesis of Si<sub>3</sub>N<sub>4</sub> from Si/NH<sub>4</sub>Cl at Low Nitrogen Pressure

Combustion synthesis of α-Si3N4 powders using in-situ nano-SiO2 coated Si and Si3N4 reactants

Combustion Synthesis of Si&lt;sub&gt;3&lt;/sub&gt;N&lt;sub&gt;4&lt;/sub&gt; from Si/NH&lt;sub&gt;4&lt;/sub&gt;Cl at Low Nitrogen Pressure

Coarse‐grained Β‐si3n4 Powders Prepared by Combustion Synthesis

On the Progress of Combustion Synthesis of Si&lt;sub&gt;3&lt;/sub&gt;N&lt;sub&gt;4&lt;/sub&gt; Ceramic: From Laboratory Research to Industrial Production

On the Progress of Combustion Synthesis of Si3n4 Ceramic: from Laboratory Research to Industrial Production

Combustion Synthesis of AlN–SiC Solid Solution Particles

Synthesis of Si3N4–TiN–SiC Composites by Combustion Reaction under High Nitrogen Pressures

Coarse‐grained β‐Si 3 N 4 powders prepared by combustion synthesis

Studies of synthesizing the SiC nanometer powders by chemical vapor reaction

Synthesis of Silicon Nitride/Silicon Carbide Nanocomposite Powders through Partial Reduction of Silicon Nitride by Pyrolyzed Carbon

Combustion synthesis Si3N4 powders by using activation process

Combustion synthesis of well-dispersed rod-like -Si<sub>3</sub>N<sub>4</sub> crystals by the addition of carbon

Effect of Nitrogen Pressure and Additives on Combustion Synthesis of Rod-Like Yttrium α-SiAlON Crystals

Effects of Pelletization of Reactants and Diluents on the Combustion Synthesis of Si3N4 Powder

Synthesis of nanocrystalline silicon carbide powders

Combustion Synthesis of Si<sub>3</sub>N<sub>4</sub> from Si/NH<sub>4</sub>Cl at Low Nitrogen Pressure

On the Progress of Combustion Synthesis of Si<sub>3</sub>N<sub>4</sub> Ceramic: From Laboratory Research to Industrial Production