Abstract:The transformation-assisted consolidation under pressure has been demonstrated to be a promising method to fabricate the nano or submicron polycrystalline ceramic materials. The high pressure suppresses the long-range diffusion of the atoms and, consequently, restrains the grain coarsening. The new phases produced at high pressure could show finer grains under the appropriate thermodynamic conditions, which are not subject to the grain size of the raw materials. Ceramic materials exhibit the existence of the transformations under certain thermodynamic conditions and the formation of new phases generally undergoes the nucleation and growth. In the present work, monoclinic microcrystal ZrO2 with average grain size of 2 µm and Y2O3 with average grain size of 50 nm were mixed in molar ratio of 97∶3. The preparation of the samples was carried out by sintering at 5.5 GPa and temperatures of 800–1700 °C using the high pressure cubic cell, and the sample characterization was performed via the X-ray diffraction, scanning electron microscope and transmission electron microscopy. It was found that the monoclinic and submicron tetragonal composite polycrystalline ZrO2 in bulk is obtained under high pressure and high temperature. The average grain size of tetragonal ZrO2 fabricated at 1200, 1400, 1600 and 1700 °C is (145±62) nm, (246±165) nm, (183±62) nm and (245±107) nm, respectively. The synthesis of the fine-grained polycrystalline materials by the transformation under high pressure can solve the problems of agglomeration, adsorption and grain coarsening caused by the nanopowders as the starting materials in the conventional approach, which would be an alternative route to fabricate the fine-grained polycrystalline materials with the enhanced performances.

High-pressure Synthesis of High-Performance Submicron-Sized Polycrystalline Β-Si3n4 Bulk Without Additives

Fabrication of Submicron Tetragonal Polycrystalline ZrO2 by the Transformation of Micro Monoclinic ZrO2 under High Pressure

Optimization of Microstructure to Improve Si3n4 Ceramics with Thermal Conductivity and Mechanical Properties: Effect of Si and Α-Si3n4 Powder Composition

Synthesis of Novel Superhard Materials under Ultrahigh Pressure

High-pressure Preparation of Bulk Tungsten Material with Near-Full Densification and High Fracture Toughness

New Route to Improve the Fracture Toughness and Flexural Strength of Si3N4 Ceramics by Adding FeSi2

Highly dense β-SiC ceramics with submicron grains prepared by sintering of nanocrystalline powders

High‐Pressure Synthesis of Amorphous Si3N4 and SiBN‐based Monoliths Without Sintering Additives

Nanocrystalline Cubic Silicon Carbide: A Route to Superhardness

Enhanced thermal shock resistance of BN-based composites sintered by hot-pressing with the introduction of nano oxides

Crystallization Behavior of Amorphous Si2bc3n Ceramic Monolith Subjected to High Pressure

Sintering pure polycrystalline boron carbide bulks with enhanced hardness and toughness under high pressure

Transparent β-Si 3 N 4 and γ-Si 3 N 4 compacts synthesized with mixed-size precursor under high pressure and high temperature

Synthesis and Growth Mechanism of Approximate Spherical Β‐si3n4 Particles Via Carbothermal Reduction‐nitridation Method

Microstructure and Performance of Silicon Nitride Ceramics with Lu2O3 Additives

Densification and Enhancement of Sic Particulate Reinforced Fine Grain Sic Ceramic

Low temperature fabrication of highly dense α‐Si3N4 ceramics

Synthesis and Growth Mechanism of Single Crystal Β‐si3n4 Particles with a Quasi‐spherical Morphology

Simultaneous improvement in porosity and strength of porous β-Si3N4 ceramics by formation of ultrafine fibrous grains

The impact of Si3N4 incorporation on the mechanical characteristics of ZrB2-SiC nanocomposite sintered via pressureless method

Microstructure and Fracture Behavior of Β-Si3n4 Based Nanoceramics