Abstract:Silicon carbide (SiC) is an effective material for high-temperature engineering applications owing to its desirable properties such as high elastic modulus, high hardness, and melting temperature, high thermal conductivity, good corrosion and oxidation resistance, low density, and coefficient of thermal expansion compared with other advanced ceramics. Nevertheless, poor sinterability and low toughness limit its use, which can be overcome using appropriate additives. In this study, the effect of different amounts of nano-β-SiC (0, 5, 10, and 15 wt.%) and graphene (0, 1, 2, and 3 wt.%) particles on the sinterability behavior and microstructure of SiC composite has been investigated. After weighing, dispersing nano-β-SiC and graphene, and mixing the starting materials, milling was carried out at 180 rpm for 3 h. The materials obtained were then compressed uniaxially under a pressure of 75 MPa and then were compressed again through CIP under 150 MPa. To remove volatile products, the pyrolysis process was performed at 800 °C under Ar atmosphere. Finally, the samples were sintered at 2200 °C for 2 h by the pressureless sintering process. XRD analysis was used to investigate the phases and FESEM images were used to study the microstructure. According to the XRD patterns, β-SiC particles were converted to α-SiC, which was accompanied by the elongation of SiC grains. Also, no reaction was observed between graphene and the SiC matrix. According to the FESEM images, the samples containing 5 wt.% nano-β-SiC and 1 wt.% graphene showed a uniform distribution of reinforcement particles but with increasing the amount of the reinforcement particles, agglomeration was observed. According to the results, upon increasing the nano-β-SiC up to 5 wt% and graphene up to 1 wt.%, all the measured properties including relative density, and linear shrinkage improved and reached 99.04%, and 18.01%, respectively. However, with increasing the additives, these properties deteriorated due to increasing porosity and agglomeration in the composite structure.

Densification and Enhancement of Sic Particulate Reinforced Fine Grain Sic Ceramic

Optimization of Microstructure to Improve Si3n4 Ceramics with Thermal Conductivity and Mechanical Properties: Effect of Si and Α-Si3n4 Powder Composition

Enhanced strength and toughness of SiC/C composite ceramics via SiC@graphene core–shell nanoparticles

Preparation Of Sic Ceramics By Spark Plasma Sintering

Porous SiC Ceramics with Controllable Porosity Achieved by Micro-sized Powder through Recrystallization Sintering

PRESSURELESS SINTERING OF SILICON CARBIDE NANOCOMPOSITE CERAMICS

Carbothermally prepared nanophase SiC/ Si3N4 composite powders and densified parts

Microstructure And Mechanical Properties Of Sic Ceramic Toughened With Tin Nanoparticles

Preparation of Porous Si2N2O/SiC Ceramics by Microwave Sintering

Microwave Sintering of Alumina-Silicon Carbide Nanocomposites

Processing and mechanical properties of B4C-SiCw ceramics densified by spark plasma sintering

Microstructure and Mechanical Properties of SiC-GNPS-SiCW Ceramics by Oscillatory Pressure Sintering

Mechanical Properties and Microstrutures of Nano-Sized Sic Particles Reinforced Az91d Nanocomposites Fabricated by High Intensity Ultrasonic Assisted Casting

Fabrication, Microstructural Evolution, and Mechanical Properties of SiC/(Hf0.25Ta0.25Zr0.25Nb0.25)C/C Nanocomposites

Synthesis and Consolidation of Composite Materials in the SiC–Si3N4–Si2N2O System

Synergistic Reinforcement of Si3N4 Based Ceramics Fabricated via Multiphase Strengthening under Low Temperature and Short Holding Time

Pressureless sintering of SiC matrix composites reinforced with nano-β-SiC and graphene

Investigation of the effect of pressure, sintering temperature and time on silicon carbide microstructure

Influence of characteristic parameters of SiC reinforcements on mechanical properties of AlSi10Mg matrix composites by powder metallurgy

Effect of In Situ Grown SiC Nanowires on the Pressureless Sintering of Heterophase Ceramics TaSi2-TaC-SiC

Fabrication and Characterization of Sic Rod-Particulate-Reinforced Reaction-Bonded Si3n4 Composites