Abstract:Features peculiar to the synthesis of SiC–Si 3 N 4 –Si 2 N 2 O composite powder with a controlled content of silicon carbide, nitride, and oxynitride phases, as well as the structure and properties of hot-pressed ceramics produced from this powder, were examined. The optimal composition of the synthesized SiC–Si 3 N 4 –Si 2 N 2 O powder was achieved by heating a 1 : 3 mixture of thermally expanded graphite (TEG) and silicon up to 1200°C in air. The interaction of TEG with fine silicon at 1200°C led to the formation of a solid solution of carbon in silicon carbide, accompanied by heat release. The generated heat increased temperature within localized volumes of the TEG cellular structure to a level where air nitrogen facilitated the development of silicon nitride and oxynitride and an amorphous phase. The amorphous phase crystallized as the interaction time increased to 2.5 h. The duration of the process influenced the final distribution of the phases, formed with the participation of CO, SiO, and air nitrogen. The microstructure of the synthesized powder was characterized by a general agglomerated state, resulting from rod and plate forms of Si 3 N 4 and Si 2 N 2 O. Hot pressing of the synthesized SiC–Si 3 N 4 –Si 2 N 2 O composite powder with Al 2 O 3 and Y 2 O 3 activators yielded superfine ceramics, possessing enhanced hardness and fracture toughness (HV10 = 20.7 GPa and K Ic = 6.5 MPa · m 1/2 ). The structure of the ceramics sintered at 2000°C differed from those sintered at 1850°C, primarily by higher density and average grain size. The superfine state significantly influenced the abrasive wear resistance of the ceramics in dry friction conditions. The linear wear index of a sample with an average size of structural elements varying from 0.2 to 1.5 μm was 111 μm/km at a sliding speed of 1 m/sec under a load of 0.2 MPa. This was significantly lower than the linear wear index of industrial ceramics of reaction-sintered silicon carbide (RSSC), which was 232.4 μm/km.

Synthesis and Characterization of Si/SiO2/SiC Composites Through Carbothermic Reduction of Rice Husk-based Silica

Synthesis and characterization of SiC/Si3N4 composites from rice husks

Preparation of SiC Powders by Carbothermal Reduction with Bamboo Charcoal As Renewable Carbon Source

Effect of temperature on the ability to synthesize SiC from rice husks

Development of Al-SiC composite material from rice husk and its parametric assessment

Preparation of Silicon Carbide Using Bamboo Charcoal As Carbon Source

Fabrication and Mechanical Properties of SiCw(p)/SiC-Si Composites by Liquid Si Infiltration using Pyrolysed Rice Husks and SiC Powders as Precursors

Reactive infiltration processing of SiC/Fe-Si composites using preforms made of coked rice husks and SiC powder

SiC whisker reinforced multi-carbides composites prepared from B4C and pyrolyzed rice husks via reactive infiltration

Coproduction of silicon nitride & oxynitride whiskers and precipitated silica from industrial rice husk ash

Synthesis of Silicon Nitride/Silicon Carbide Nanocomposite Powders through Partial Reduction of Silicon Nitride by Pyrolyzed Carbon

Silicon Carbide-based Materials from Rice Husk

Carbothermal Reduction Behavior of Micro-silica

In-situ synthesis of SiC nanowires on biomass carbon materials derived from cherry stones

Effect of Carbonization Temperature of Rice Husk Char Preparation on SiC Structure and Composition of By-Products in SiC Synthesis with Magnesiothermic Reduction Method

INFLUENCE OF Al2O3 ON PREPARING POROUS SILICON NITRIDE BASED CERAMIC FROM RICE HUSK

Mechanical, dry sliding wear and tensile fatigue behaviour of rice hush ash–derived silicon carbide dispersed LM25 metal matrix composites

Synthesis and Consolidation of Composite Materials in the SiC–Si3N4–Si2N2O System

Preparation Of Nanocrystalline Silicon Carbide Powders By Carbothermal Reduction

Tribological Behavoiur of Silicon Carbide/ Rice Husk ash Reinforced Al7075 Hybrid Composites Using Optimization Techniques

Synthesis of nanocrystalline silicon carbide powders