Abstract:Features peculiar to the synthesis of SiC–Si 3 N 4 –Si 2 N 2 O composite powder with a controlled content of silicon carbide, nitride, and oxynitride phases, as well as the structure and properties of hot-pressed ceramics produced from this powder, were examined. The optimal composition of the synthesized SiC–Si 3 N 4 –Si 2 N 2 O powder was achieved by heating a 1 : 3 mixture of thermally expanded graphite (TEG) and silicon up to 1200°C in air. The interaction of TEG with fine silicon at 1200°C led to the formation of a solid solution of carbon in silicon carbide, accompanied by heat release. The generated heat increased temperature within localized volumes of the TEG cellular structure to a level where air nitrogen facilitated the development of silicon nitride and oxynitride and an amorphous phase. The amorphous phase crystallized as the interaction time increased to 2.5 h. The duration of the process influenced the final distribution of the phases, formed with the participation of CO, SiO, and air nitrogen. The microstructure of the synthesized powder was characterized by a general agglomerated state, resulting from rod and plate forms of Si 3 N 4 and Si 2 N 2 O. Hot pressing of the synthesized SiC–Si 3 N 4 –Si 2 N 2 O composite powder with Al 2 O 3 and Y 2 O 3 activators yielded superfine ceramics, possessing enhanced hardness and fracture toughness (HV10 = 20.7 GPa and K Ic = 6.5 MPa · m 1/2 ). The structure of the ceramics sintered at 2000°C differed from those sintered at 1850°C, primarily by higher density and average grain size. The superfine state significantly influenced the abrasive wear resistance of the ceramics in dry friction conditions. The linear wear index of a sample with an average size of structural elements varying from 0.2 to 1.5 μm was 111 μm/km at a sliding speed of 1 m/sec under a load of 0.2 MPa. This was significantly lower than the linear wear index of industrial ceramics of reaction-sintered silicon carbide (RSSC), which was 232.4 μm/km.

Synthesis and characterization of SiC/Si3N4 composites from rice husks

Synthesis and Characterization of Si/SiO2/SiC Composites Through Carbothermic Reduction of Rice Husk-based Silica

Silicon Carbide-based Materials from Rice Husk

Effect of temperature on the ability to synthesize SiC from rice husks

INFLUENCE OF Al2O3 ON PREPARING POROUS SILICON NITRIDE BASED CERAMIC FROM RICE HUSK

Coproduction of silicon nitride & oxynitride whiskers and precipitated silica from industrial rice husk ash

Silicon oxycarbide composites reinforced with silicon nitride and in situ formed silicon carbide.

Synthesis and properties of porous SiN/SiC nanocomposites by carbothermal reaction between SiN and carbon

SiC whisker reinforced multi-carbides composites prepared from B4C and pyrolyzed rice husks via reactive infiltration

Fabrication and Mechanical Properties of SiCw(p)/SiC-Si Composites by Liquid Si Infiltration using Pyrolysed Rice Husks and SiC Powders as Precursors

Mesoporous Silica with an Alveolar Construction Obtained by Eco-Friendly Treatment of Rice Husks

Cost-effective Production of SiO2/C and Si/C Composites Derived from Rice Husk for Advanced Lithium-Ion Battery Anodes

Synthesis and Consolidation of Composite Materials in the SiC–Si3N4–Si2N2O System

Hybrid one-dimensional nanostructure based on biomorphic porous SiO 2 through in-situ catalytic pyrolysis of rice husk

Synthesis of Silicon Nitride/Silicon Carbide Nanocomposite Powders through Partial Reduction of Silicon Nitride by Pyrolyzed Carbon

Preparation and Characterization of Rice Husk/Ferrite Composites

Development of Al-SiC composite material from rice husk and its parametric assessment

Studying the kinetics of extraction treatment of rice husk when obtaining silicon carbide

Processing and properties of nanophase SiC/Si3N4 composites

Fabrication Of Sio2 Porous Ceramics From Rice Husk Ash

Fabrication of SiO<sub>2</sub> Porous Ceramics from Rice Husk Ash