Abstract:An innovative process for preparing silicon carbide (SiC) from acid leaching residue of ferronickel slag through a carbon–thermal reduction process was proposed in this study. The results indicate that the acid leaching residue is an ideal silicon source for SiC preparation according to its high amorphous silica content of 84.20% and fine particle size of d50 = 29.16 μm. Compared with carbon black, activated carbon, and graphite, coke is the more appropriate carbon source for SiC preparation. A micron-size SiC powder with grade of 88.90% and an average particle size (d50) of 44.68 μm can be obtained under the following conditions: the mass ratio of coke to leaching residue as 1.2:1, in an air atmosphere, reducing at 1600 °C for 3 h, following by decarbonizing at 700 °C for 4 h. The XRD, SEM and FTIR analyses show that the prepared powder is 3C-SiC and belongs to the β-SiC crystal type. Based on thermodynamic analysis and micromorphology observation, it can be concluded that with amorphous silica as the silicon source, the carbon–thermal synthesis of SiC powder follows both the solid–solid reaction mechanism and the gas–solid mechanism. The SiC created through solid–solid reaction is primarily nucleated in situ on amorphous SiO2, with a size close to that of the original acid-leaching slag, while the SiC generated according to the gas–solid mechanism mainly nucleates heterogeneously on the surface of carbon particles, resulting in a smaller particle size and mostly adhering to the surface of solid–solid nucleated SiC particles. This study provides a feasible method for the effective utilization of amorphous silica, which is also significant for the efficient consumption of the vast acid leaching residue.

Preparation of Silicon Carbide Using Bamboo Charcoal As Carbon Source

Preparation of SiC Powders by Carbothermal Reduction with Bamboo Charcoal As Renewable Carbon Source

Preparation of Porous SiC Ceramic Using Bamboo Charcoal and Silica Sol As Pore-Forming Agents

Effects of Additives on the Microstructure of Synthesized Sic Particles by Using Silica Sol/Bamboo Charcoal System

In-situ synthesis of SiC nanowires on biomass carbon materials derived from cherry stones

Preparation of β-Sialon /SiC composite powder by carbothermal reaction of coal-mine schist

Synthesis and Characterization of Si/SiO2/SiC Composites Through Carbothermic Reduction of Rice Husk-based Silica

Preparation of Silicon Carbide Powder from Amorphous Silica and Investigation of Synthesis Mechanism

Theoretical and experimental study of the mechanism for preparation of SiC nanowires by carbothermal reduction

Controlled growth of SiC crystals in combustion synthesis

Preparation Of Nanocrystalline Silicon Carbide Powders By Carbothermal Reduction

Preparation of beta sialon/SiC composite powder by carbothermal reaction of coal mine schist

Synthesis of nanocrystalline silicon carbide powders

Preparation of SiC/Si3N4 composites with rod-like microstructure by combustion synthesis

Synthesis and characterization of submicron silicon carbide powders with silicon and phenolic resin

Low-temperature formation of nanocrystalline β-SiC with high surface area and mesoporosity via reaction of mesoporous carbon and silicon powder

Synthesis of High Purity SiC Powder for High-resistivity SiC Single Crystals Growth

Advanced Arc Plasma Synthesis of Biomorphic Silicon Carbide Using Charcoal and Silicon Dioxide in Air

Preparation of Hierarchical Porous Silicon Carbide Monoliths via Ambient Pressure Drying Sol–Gel Process Followed by High-Temperature Pyrolysis

High Yield Silicon Carbide Whiskers from Rice Husk Ash and Graphene: Growth Method and Thermodynamics

Preparation and mechanical behaviors of multiscale SiC nanowires/carbon fiber reinforced silicon oxycarbide ceramic composites