Preparation Of Nanocrystalline Zirconium Carbide Powders By Carbothermal Reduction

A Jain,Md Sacks,Ca Wang
2003-01-01
Abstract:Zirconium carbide (ZrC) powders were produced by the carbothermal reduction reaction of zirconia and carbon. Solution-based processing was used to achieve a fine-scale mixing of the reactants. The reaction was substantially completed at relatively low temperature (1400degreesC) and the resulting ZrC product had small average crystallite size (similar to120 nm). ZrC powder compacts were pressureless sintered to >90% relative density at 1800degreesC.